PET Rynite 530 BK503

30% Glass Reinforced Polyethylene Terephthalate

Information provided by DuPont. This product line has remained with DuPont after the DuPont-Dow merger.

Physical Properties	Metric	English	Comments
Density	1.56 g/cc	0.0564 lb/in3	ISO 1183
Linear Mold Shrinkage, Flow	0.0030 cm/cm	0.0030 in/in	ISO 294-4, 2577
Linear Mold Shrinkage, Transverse	0.0090 cm/cm	0.0090 in/in	ISO 294-4, 2577
Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	150 MPa	21800 psi	ISO 527-1/-2
Elongation at Break	2.1 %	2.1 %	ISO 527-1/-2
Tensile Modulus	10.2 GPa	1480 ksi	ISO 527-1/-2
Flexural Strength	210 MPa	30500 psi	ISO 178
Flexural Modulus	8.94 GPa	1300 ksi	ISO 178
Poissons Ratio	0.34	0.34	ISO 527-1/-2
Izod Impact, Notched (ISO)	35.0 kJ/m2 @Temperature -40.0 °C	16.7 ft-lb/in2 @Temperature -40.0 °F	ISO 180/1U
	45.0 kJ/m2 @Temperature 23.0 °C	21.4 ft-lb/in2 @Temperature 73.4 °F	ISO 180/1U

PET Rynite 530 BK503

性能

PET是乳白色或浅黄色高度结晶性的聚合物，表面平滑而有光泽。耐蠕变、耐抗疲劳性、耐磨擦和尺寸稳定性好，磨耗小而硬度高，具有热塑性塑料中最大的韧性：电绝缘性能好，受温度影响小，但耐电晕性较差。无毒、耐气候性、抗化学药品稳定性好，吸水率低，耐弱酸和有机溶剂，但不耐热水浸泡，不耐碱。

PET树脂的玻璃化温度较高，结晶速度慢，模塑周期长，成型周期长，成型收缩率大，尺寸稳定性差，结晶化的成型呈脆性，耐热性低等。

通过成核剂以及结晶剂和玻璃纤维增强的改进，PET除了具有PBT的性质外，还有以下的特点。

1.热变形温度和长期使用温度是热塑性通用工程塑料中最高的

2.因为耐热高，增强PET在250℃的焊锡浴中浸渍10S，几乎不变形也不变色，特别适合制备锡焊的电子、电气零件。

3.弯曲强度 200MPa,弹性模量达4000MPa，耐蠕变及疲劳性也很好，表面硬度高，机械性能与热固性塑料相近。

4.由于生产PET所用乙二醇比生产PBT所用丁二醇的价格几乎便宜一半，所以PET树脂和增强PET是工程塑料中价格最低的，具有很高的性价比。

用途

在塑料分类中，PET的代号是1号，作用广泛：

主要应用为电子电器方面有：电气插座、电子连接器、电饭煲把手、电视偏向轭，端子台，断电器外壳、开关、马达风扇外壳、仪表机械零件、点钞机零件、电熨斗、电磁灶烤炉的配件；汽车工业中的流量控制阀、化油器盖、车窗控制器、脚踏变速器、配电盘罩；机械工业齿轮、叶片、皮带轮、泵零件、另外还有轮椅车体及轮子、灯罩外壳、照明器外壳、排水管接头、拉链、钟表零件、喷雾器部件。

另外：

可纺成聚酯纤维，即涤纶。

可制成薄膜用于录音、录像、电影胶片等的基片、绝缘膜、产品包装等。

作为塑料可吹制成各种瓶，如可乐瓶、矿泉水瓶等。

可作为电器零部件、轴承、齿轮等。

PET Rynite 530 BK503 可提供COA、COC,ROHS.MSDS.UL黄卡等等资料，价格最优，质量保证！