东莞市常平山鑫塑胶原料经营部
我公司长期供应PC如下型号
沙特沙伯基础
LEXAN FL1000 PC
LEXAN FL2000 PC
LEXAN FL2003 PC
LEXAN FL3000 PC
LEXAN FL403 PC
LEXAN FL405 PC
LEXAN FL410 PC
LEXAN FL900 PC
LEXAN FL900S PC
LEXAN FL903 PC
LEXAN FL910 PC
LEXAN FL913 PC
LEXAN FL920 PC
LEXAN FL930 PC
LEXAN FL933 PC
LEXAN FST9705 PC
LEXAN FXD101R PC
LEXAN FXD103 PC
LEXAN FXD103R PC
LEXAN FXD104R PC
通用塑料：
ABS ABS高胶粉 ADPOLY AS(SAN) EPS MABS CA CAB EAA EVA GPPS HDPE HIPS K(Q)胶 K胶 LDPE LLDPE MBS MDPE MS MVLDPE(茂金属) PET PE蜡 PMMA PP PVC ULDPE
工程塑料：
ASA PA6 PA66 PBT PC PC/ABS PCTA PCTG PETG POM
特种工程塑料：
AES APPEEL CAP COC COP CPVC DAP EBA ECTFE EEA EFEP EMAA ETFE EVOH EXACT FEP LCBR LCP MMBS PA1010 PA10T PA11 PA12 PA46 PA4T PA610 PA612 PA6T PA9T PAE PAR PARA PB-1 PCT PEEK PEI PES PF PFA PMP POK PPA PPE PPO PP-B PP-R PPS PPSU PPTA PSU PTFE PVDF SEPS SMA树脂 SMMA SOE SPS THV UCAR UHMWPE XLPE
合金塑料：
ABS/PA ABS/PBT ABS/PC ABS/PMMA ASA/PC M/PE/PP PA1212/PTFE PA12/PTFE PA612/F/PTFE PA6/66 PA610/PTFE PA66/C/PTFE PA66/CF PA66/F/PTFE PA66/PTFE PA6T/66 PA/ABS PA/MXD6 PBT/ABS PBT/ASA PBT/F/PTFE PBT/PC PBT/PET PC/AES PC/ASA PC/C/PTFE PC/CF PC/HIPS PC/PBT PC/PET PC/PMMA PC/PS PC/PTFE PC/SANPC/TPFE PCTA/PCTG PE/PTFE POM/PTFE PPE/PA PPO/PA PPS/CF
热塑弹性体：
BR EMA EMMA CPE OBC POE PBE POP SBR SBS SEBS SURLYN SIS SSBR TPE TPEE TPO TPR TPSIV TPU TPV 氟橡胶 硅胶 丁二烯橡胶 丁腈橡胶
SABIC Innovative Plastics Lexan® FXD103 PC 物性表
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | 1.20 g/cc | 1.20 g/cc | ASTM D 792 |
| 密度 | 1.20 g/cc | 0.0434 lb/in3 | ISO 1183 |
| 平衡吸湿 | 0.15 % | 0.15 % | 23°C / 50% RH; ISO 62 |
| 饱和吸水率 | 0.35 % @Temperature 23.0 °C |
0.35 % @Temperature 73.4 °F |
ISO 62 |
| 线性成型收缩率,Flow | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | on tensile bar; SABIC Method |
| 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method | |
| 熔体流动速率 | 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
6.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
| 7.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
7.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D 1238 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(断裂) | 66.0 MPa | 9570 psi | Type I, 50 mm/min; ASTM D 638 |
| 70.0 MPa | 10200 psi | 50 mm/min; ISO 527 | |
| 抗张强度(屈服) | 62.0 MPa | 8990 psi | Type I, 50 mm/min; ASTM D 638 |
| 63.0 MPa | 9140 psi | 50 mm/min; ISO 527 | |
| 伸长率 (断裂) | 110 % | 110 % | Type I, 50 mm/min; ASTM D 638 |
| 120 % | 120 % | 50 mm/min; ISO 527 | |
| 屈服伸长率 | 6.0 % | 6.0 % | 50 mm/min; ISO 527 |
| 7.0 % | 7.0 % | Type I, 50 mm/min; ASTM D 638 | |
| 拉伸模量 | 2.34 GPa | 339 ksi | 5 mm/min; ASTM D 638 |
| 2.35 GPa | 341 ksi | 1 mm/min; ISO 527 | |
| 弯曲强度 | 90.0 MPa | 13100 psi | 2 mm/min; ISO 178 |
| 93.0 MPa | 13500 psi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| 弯曲模量 | 2.30 GPa | 334 ksi | 2 mm/min; ISO 178 |
| 2.34 GPa | 339 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| 悬壁梁缺口冲击强度 | 1.44 J/cm @Temperature -30.0 °C |
2.70 ft-lb/in @Temperature -22.0 °F |
ASTM D 256 |
| 9.08 J/cm @Temperature 23.0 °C |
17.0 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 | |
| 悬壁梁无缺口冲击强度 | 32.04 J/cm @Temperature 23.0 °C |
60.02 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| 悬壁梁缺口冲击强度 | 10.0 kJ/m2 @Temperature -30.0 °C |
4.76 ft-lb/in2 @Temperature -22.0 °F |
80*10*4; ISO 180/1A |
| 12.0 kJ/m2 @Temperature -30.0 °C |
5.71 ft-lb/in2 @Temperature -22.0 °F |
80*10*3; ISO 180/1A | |
| 65.0 kJ/m2 @Temperature 23.0 °C |
30.9 ft-lb/in2 @Temperature 73.4 °F |
80*10*4; ISO 180/1A | |
| 70.0 kJ/m2 @Temperature 23.0 °C |
33.3 ft-lb/in2 @Temperature 73.4 °F |
80*10*3; ISO 180/1A | |
| 悬壁梁无缺口冲击强度 | NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
80*10*3; ISO 180/1U |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
80*10*3; ISO 180/1U | |
| 简支梁无缺口冲击强度 | NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
Edgew 80*10*3 sp=62mm; ISO 179/1eU |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
Edgew 80*10*3 sp=62mm; ISO 179/1eU | |
| 简支梁缺口冲击强度 | 1.50 J/cm2 @Temperature -30.0 °C |
7.14 ft-lb/in2 @Temperature -22.0 °F |
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA |
| 7.50 J/cm2 @Temperature 23.0 °C |
35.7 ft-lb/in2 @Temperature 73.4 °F |
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA | |
| 冲击试验 | 68.0 J @Temperature 23.0 °C |
50.2 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线形热膨胀系数 - 流动 | 70.0 μm/m-°C @Temperature -40.0 - 95.0 °C |
38.9 μin/in-°F @Temperature -40.0 - 203 °F |
ASTM E 831 |
| 71.7 μm/m-°C @Temperature 23.0 - 80.0 °C |
39.8 μin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 | |
| 线性热膨胀系数,横向流动 | 71.0 μm/m-°C @Temperature -40.0 - 95.0 °C |
39.4 μin/in-°F @Temperature -40.0 - 203 °F |
ASTM E 831 |
| 72.7 μm/m-°C @Temperature 23.0 - 80.0 °C |
40.4 μin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 | |
| 载荷下热变形温度(0.46 MPa) | 138 °C | 280 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| 138 °C @Thickness 3.20 mm |
280 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| 载荷下热变形温度(1.8 MPa) | 127 °C | 261 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| 132 °C @Thickness 3.20 mm |
270 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| 维卡软化温度 | 144 °C | 291 °F | Rate B/50; ISO 306 |
| 145 °C | 293 °F | Rate B/120; ISO 306 | |
| 154 °C | 309 °F | Rate B/50; ASTM D 1525 | |
| 可燃性(UL94) | HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
UL 94 by SABIC-IP |
| 材料描述 | 测试方法 | |
|---|---|---|
| Ball Pressure Test, 75°C +/- 2°C | Pass | IEC 60695-10-2 |