SABIC Innovative Plastics Lexan® EXRL0672 PC Copolymer 物性表
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | 1.20 g/cc | 1.20 g/cc | ASTM D 792 |
| 密度 | 1.20 g/cc | 0.0434 lb/in3 | ISO 1183 |
| 1.20 g/cc | 0.0434 lb/in3 | ASTM D 792 | |
| 平衡吸湿 | 0.15 % | 0.15 % | 23°C / 50% RH; ISO 62 |
| 饱和吸水率 | 0.30 % @Temperature 23.0 °C |
0.30 % @Temperature 73.4 °F |
ISO 62 |
| 线性成型收缩率,Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| 熔体流动速率 | 38 g/10 min @Load 1.20 kg, Temperature 300 °C |
38 g/10 min @Load 2.65 lb, Temperature 572 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
| 40 g/10 min @Load 1.20 kg, Temperature 300 °C |
40 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D 1238 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 洛氏硬度（R 级） | 120 | 120 | ASTM D 785 |
| 抗张强度(断裂) | 56.0 MPa | 8120 psi | Type I, 50 mm/min; ASTM D 638 |
| 56.0 MPa | 8120 psi | 50 mm/min; ISO 527 | |
| 抗张强度(屈服) | 60.0 MPa | 8700 psi | Type I, 50 mm/min; ASTM D 638 |
| 63.0 MPa | 9140 psi | 50 mm/min; ISO 527 | |
| 伸长率 (断裂) | 97 % | 97 % | 50 mm/min; ISO 527 |
| 130 % | 130 % | Type I, 50 mm/min; ASTM D 638 | |
| 屈服伸长率 | 5.5 % | 5.5 % | Type I, 50 mm/min; ASTM D 638 |
| 6.0 % | 6.0 % | 50 mm/min; ISO 527 | |
| 拉伸模量 | 2.18 GPa | 316 ksi | 1 mm/min; ISO 527 |
| 2.27 GPa | 329 ksi | 5 mm/min; ASTM D 638 | |
| 弯曲强度 | 91.0 MPa | 13200 psi | 2 mm/min; ISO 178 |
| 100 MPa | 14500 psi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| 弯曲模量 | 2.18 GPa | 316 ksi | 2 mm/min; ISO 178 |
| 2.24 GPa | 325 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| 悬壁梁缺口冲击强度 | 6.99 J/cm @Temperature 0.000 °C |
13.1 ft-lb/in @Temperature 32.0 °F |
ASTM D 256 |
| 7.28 J/cm @Temperature 23.0 °C |
13.6 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 | |
| 11.0 kJ/m2 @Temperature -30.0 °C |
5.23 ft-lb/in2 @Temperature -22.0 °F |
80*10*3; ISO 180/1A | |
| 58.0 kJ/m2 @Temperature 23.0 °C |
27.6 ft-lb/in2 @Temperature 73.4 °F |
80*10*3; ISO 180/1A | |
| 悬壁梁无缺口冲击强度 | NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
80*10*3; ISO 180/1U |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
80*10*3; ISO 180/1U | |
| 简支梁无缺口冲击强度 | NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
Edgew 80*10*3 sp=62mm; ISO 179/1eU |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
Edgew 80*10*3 sp=62mm; ISO 179/1eU | |
| 简支梁缺口冲击强度 | 1.30 J/cm2 @Temperature -30.0 °C |
6.19 ft-lb/in2 @Temperature -22.0 °F |
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA |
| 6.40 J/cm2 @Temperature 23.0 °C |
30.5 ft-lb/in2 @Temperature 73.4 °F |
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA | |
| 冲击试验 | 95.0 J | 70.1 ft-lb | Multiaxial Impact; ISO 6603 |
| 56.0 J @Temperature 23.0 °C |
41.3 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线形热膨胀系数 - 流动 | 80.0 μm/m-°C @Temperature -40.0 - 40.0 °C |
44.4 μin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 80.0 μm/m-°C @Temperature -40.0 - 40.0 °C |
44.4 μin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| 线性热膨胀系数,横向流动 | 80.0 μm/m-°C @Temperature -40.0 - 40.0 °C |
44.4 μin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 80.0 μm/m-°C @Temperature -40.0 - 40.0 °C |
44.4 μin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| 载荷下热变形温度(0.46 MPa) | 121 °C @Thickness 3.20 mm |
250 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| 载荷下热变形温度(1.8 MPa) | 115 °C | 239 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 110 °C @Thickness 3.20 mm |
230 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| 维卡软化温度 | 129 °C | 264 °F | Rate B/50; ISO 306 |
| 130 °C | 266 °F | Rate B/120; ISO 306 | |
| 135 °C | 275 °F | Rate B/50; ASTM D 1525 |
| 光学性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 折射率 | 1.582 | 1.582 | ASTM D 542 |
| 雾度 | <= 1.0 % @Thickness 2.54 mm |
<= 1.0 % @Thickness 0.100 in |
ASTM D 1003 |
| Transmission, Visible | 88 % @Thickness 2.54 mm |
88 % @Thickness 0.100 in |
ASTM D 1003 |
| 材料描述 | 测试方法 | |
|---|---|---|
| 球压试验，125°C+/-2℃ | PASS | IEC 60695-10-2 |