我公司长期供应PC如下型号
基础创新塑料
LEXAN EXL1033C PC
LEXAN EXL1036 PC
LEXAN EXL1112 PC
LEXAN EXL1112T PC
LEXAN EXL1132 PC
LEXAN EXL1132T PC
LEXAN EXL1162T PC
LEXAN EXL1182T PC
LEXAN EXL1192C PC
LEXAN EXL1192T PC
LEXAN EXL1330 PC
LEXAN EXL1413T PC
LEXAN EXL1414 PC
LEXAN EXL1414H PC
LEXAN EXL1414T PC
LEXAN EXL1433T PC
LEXAN EXL1434 PC
LEXAN EXL1434T PC
LEXAN EXL1443T PC
LEXAN EXL1444 PC
LEXAN EXL1463T PC
LEXAN EXL1464T PC
LEXAN EXL1483T PC
LEXAN EXL1484T PC
LEXAN EXL1493T PC
LEXAN EXL1494T PC
LEXAN EXL1810T PC
LEXAN EXL1860T PC
LEXAN EXL1880T PC
LEXAN EXL1890T PC
通用塑料:
ABS ABS高胶粉 ADPOLY AS(SAN) EPS MABS CA CAB EAA EVA GPPS HDPE HIPS K(Q)胶 K胶 LDPE LLDPE MBS MDPE MS MVLDPE(茂金属) PET PE蜡 PMMA PP PVC ULDPE
工程塑料:
ASA PA6 PA66 PBT PC PC/ABS PCTA PCTG PETG POM
特种工程塑料:
AES APPEEL CAP COC COP CPVC DAP EBA ECTFE EEA EFEP EMAA ETFE EVOH EXACT FEP LCBR LCP MMBS PA1010 PA10T PA11 PA12 PA46 PA4T PA610 PA612 PA6T PA9T PAE PAR PARA PB-1 PCT PEEK PEI PES PF PFA PMP POK PPA PPE PPO PP-B PP-R PPS PPSU PPTA PSU PTFE PVDF SEPS SMA树脂 SMMA SOE SPS THV UCAR UHMWPE XLPE
合金塑料:
ABS/PA ABS/PBT ABS/PC ABS/PMMA ASA/PC M/PE/PP PA1212/PTFE PA12/PTFE PA612/F/PTFE PA6/66 PA610/PTFE PA66/C/PTFE PA66/CF PA66/F/PTFE PA66/PTFE PA6T/66 PA/ABS PA/MXD6 PBT/ABS PBT/ASA PBT/F/PTFE PBT/PC PBT/PET PC/AES PC/ASA PC/C/PTFE PC/CF PC/HIPS PC/PBT PC/PET PC/PMMA PC/PS PC/PTFE PC/SANPC/TPFE PCTA/PCTG PE/PTFE POM/PTFE PPE/PA PPO/PA PPS/CF
热塑弹性体:
BR EMA EMMA CPE OBC POE PBE POP SBR SBS SEBS SURLYN SIS SSBR TPE TPEE TPO TPR TPSIV TPU TPV 氟橡胶 硅胶 丁二烯橡胶 丁腈橡胶
SABIC Innovative Plastics Lexan® EXL1483T PC Copolymer 物性表
物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
比重 | 1.19 g/cc | 1.19 g/cc | ASTM D 792 |
密度 | 1.19 g/cc | 0.0430 lb/in3 | ISO 1183 |
平衡吸湿 | 0.090 % | 0.090 % | 23°C / 50% RH; ISO 62 |
饱和吸水率 | 0.24 % @Temperature 23.0 °C |
0.24 % @Temperature 73.4 °F |
ISO 62 |
线性成型收缩率,Flow | 0.0040 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0080 in/in @Thickness 0.126 in |
SABIC Method |
熔体流动速率 | 9.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
9.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
10 g/10 min @Load 1.20 kg, Temperature 300 °C |
10 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D 1238 |
机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
抗张强度(断裂) | 61.0 MPa | 8850 psi | 50 mm/min; ISO 527 |
64.0 MPa | 9280 psi | Type I, 50 mm/min; ASTM D 638 | |
抗张强度(屈服) | 57.0 MPa | 8270 psi | 50 mm/min; ISO 527 |
58.0 MPa | 8410 psi | Type I, 50 mm/min; ASTM D 638 | |
伸长率 (断裂) | 124.9 % | 124.9 % | 50 mm/min; ISO 527 |
131.4 % | 131.4 % | Type I, 50 mm/min; ASTM D 638 | |
屈服伸长率 | 5.5 % | 5.5 % | 50 mm/min; ISO 527 |
5.8 % | 5.8 % | Type I, 50 mm/min; ASTM D 638 | |
拉伸模量 | 2.21 GPa | 321 ksi | 50 mm/min; ASTM D 638 |
2.35 GPa | 341 ksi | 1 mm/min; ISO 527 | |
弯曲强度 | 90.0 MPa | 13100 psi | 2 mm/min; ISO 178 |
94.0 MPa | 13600 psi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
弯曲模量 | 2.15 GPa | 312 ksi | 2 mm/min; ISO 178 |
2.21 GPa | 321 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
悬壁梁缺口冲击强度 | 7.95 J/cm @Temperature -30.0 °C |
14.9 ft-lb/in @Temperature -22.0 °F |
ASTM D 256 |
8.90 J/cm @Temperature 23.0 °C |
16.7 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 | |
29.0 kJ/m2 @Temperature -30.0 °C |
13.8 ft-lb/in2 @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
56.0 kJ/m2 @Temperature 23.0 °C |
26.6 ft-lb/in2 @Temperature 73.4 °F |
80*10*4; ISO 180/1A | |
简支梁缺口冲击强度 | 2.40 J/cm2 @Temperature -30.0 °C |
11.4 ft-lb/in2 @Temperature -22.0 °F |
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA |
7.40 J/cm2 @Temperature 23.0 °C |
35.2 ft-lb/in2 @Temperature 73.4 °F |
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA | |
冲击试验 | 82.0 J @Temperature 23.0 °C |
60.5 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
线形热膨胀系数 - 流动 | 71.5 μm/m-°C @Temperature -40.0 - 95.0 °C |
39.7 μin/in-°F @Temperature -40.0 - 203 °F |
ASTM E 831 |
71.5 μm/m-°C @Temperature 23.0 - 80.0 °C |
39.7 μin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 | |
线性热膨胀系数,横向流动 | 79.3 μm/m-°C @Temperature -40.0 - 95.0 °C |
44.1 μin/in-°F @Temperature -40.0 - 203 °F |
ASTM E 831 |
79.3 μm/m-°C @Temperature 23.0 - 80.0 °C |
44.1 μin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 | |
载荷下热变形温度(1.8 MPa) | 118 °C | 244 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
124 °C @Thickness 3.20 mm |
255 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
维卡软化温度 | 141 °C | 286 °F | Rate A/50; ASTM D 1525 |
141 °C | 286 °F | Rate B/50; ISO 306 | |
142 °C | 288 °F | Rate B/120; ISO 306 |