PP MOPLEN HP456J
Moplen HP456J is a polypropylene homopolymer used for extrusion and thermoforming applications. Moplen HP456J is formulated with a low water-carry-over additive package. Typical applications are monofilaments, ropes and tapes. Applications: Raffia/Tapes/Strapping.
Information provided by LyondellBasell.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.900 g/cc | 0.0325 lb/in3 | ISO 1183-1 |
| Melt Flow | 3.4 g/10 min @Load 2.16 kg, Temperature 230 °C |
3.4 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133-1 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 23.0 MPa | 3340 psi | 50mm/min; ISO 527-1,-2 |
| Tensile Strength, Yield | 34.0 MPa | 4930 psi | 50mm/min; ISO 527-1,-2 |
| Elongation at Break | 600 % | 600 % | 50mm/min; ISO 527-1,-2 |
| Elongation at Yield | 11 % | 11 % | 50mm/min; ISO 527-1,-2 |
| Flexural Modulus | 1.40 GPa | 203 ksi | ISO 178 |
PP MOPLEN HP456J
成型特性
（1）物理性能：PP为无毒、无味的乳白色高结晶的聚合物，是目前所有塑料中最最轻的品种之一，对水特别稳定，在水中14h的吸水率仅为0.01%。分子量约8~15万之间，成型性好。但因收缩率大，原壁制品易凹陷，制品表面光泽好，易于着色。
（2）力学性能：PP的结晶度高，结构规整，因而具有优良的力学性能，其强度和硬度、弹性都比高密度PE(HDPE)高。突出特点是抗弯曲疲劳性（7×10^7）次开闭的折选弯曲而无损坏痕迹，干摩擦系数与尼龙相似，但在油润滑下不如尼龙。
（3）热性能：PP 具有良好的 耐热性，熔点在164~170℃，制品能在100℃以上温度进行消毒灭菌。在不受外力的作用下，150℃也不变形。脆化为-35℃，在低于-35℃会发生脆化。
（4）化学稳定性：PP具有良好的化学稳定性，除能被浓硫酸、浓硝酸侵蚀外，对其他各种化学试剂都比较稳定，但低分子量的脂肪烃、芳香烃等能使PP软化和溶胀，化学稳定性随结晶度的增加还有所提高。所以，PP适合制作俄中化工管道和配件，防腐蚀效果良好。
（5）电性能：聚丙烯的高频绝缘性能优良，由于它几乎不吸水，故绝缘性能不受湿度的影响，有较高的介电系数，且随温度的上升，可以用来制作受热的电气绝缘制品，击穿电压也很高，适用作电器配件等。抗 电压、耐电弧性好，但静电度高，与铜接触易老化。
（6）耐候性：聚丙烯对紫外线很敏感，加入氧化锌硫代丙酸二月桂脂，炭黑式类似的乳白填料等可以改善其耐老化性能。