ABS POLYLAC PA-747S

Physical Properties	Metric	English	Comments
Density	1.03 g/cc	0.0372 lb/in3	ISO 1183
Linear Mold Shrinkage	0.0030 - 0.0070 cm/cm	0.0030 - 0.0070 in/in	ASTM D955
Melt Flow	4.4 g/10 min @Load 5.00 kg, Temperature 230 °C	4.4 g/10 min @Load 11.0 lb, Temperature 446 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	101	101	ASTM D785
Ball Indentation Hardness	89.0 MPa	12900 psi	H358/30; ISO 2039-1
Tensile Strength at Break	30.0 MPa	4350 psi	50 mm/min; ISO 527
Tensile Strength, Yield	40.0 MPa	5800 psi	50 mm/min; ISO 527
Elongation at Break	40 %	40 %	50 mm/min; ISO 527
Flexural Strength	57.0 MPa	8270 psi	2 mm/min; ISO 178
Flexural Modulus	1.70 GPa	247 ksi	2 mm/min; ISO 178
Izod Impact, Notched	3.93 J/cm @Thickness 3.17 mm	7.36 ft-lb/in @Thickness 0.125 in
Izod Impact, Notched (ISO)	29.0 kJ/m2	13.8 ft-lb/in2	ISO 180/1A
Izod Impact, Unnotched (ISO)	NB	NB	ISO 180/1C
Charpy Impact Unnotched	NB	NB	ISO 179
Charpy Impact, Notched	3.10 J/cm2	14.8 ft-lb/in2	ISO 179
Impact	19	19	Impact Flexural Test Notched (KJ/m2)
	NB	NB	Impact Flexural Test Unnotched (KJ/m2

ABS POLYLAC PA-747S 可提供COA、COC,ROHS.MSDS.UL黄卡等等资料，价格最优，质量保证！

特性：

ABS同PS一样是一种加工性能优良的热塑性塑料，可用通用的加工方法加工。 ABS的熔体流动性比PVC和PC好，但比PE、PA及PS差，与POM和HIPS类似；ABS的流动特性属非牛顿流体，其熔体粘度对加工温度和剪切速率都有关系，但对剪切速率更为敏感。

ABS的热稳定性好，不易出现降解现象。ABS的吸水性较高，加工前应进行干燥处理。一般制品的干燥条件为温度80~85℃，时间2~4h；对特殊要求的制品（如电镀）的干燥条件为温度70~80℃，时间18~18h。 ABS制品在加工中易产生内应力，内应力的大小可通过浸入冰乙酸中检验；如应力太大和制品对应力开裂绝对禁止，应进行退火处理，具体条件为放于70~80℃的热风循环干燥箱内2~4h，再冷却至室温即可。

用途：

ABS树脂的最大应用领域是汽车、电子电器和建材。汽车领域的使用包括汽车仪表板、车身外板、内装饰板、方向盘、隔音板、门锁、保险杠、通风管等很多部件。在电器方面则广泛应用于电冰箱、电视机、洗衣机、空调器、计算机、复印机等电子电器中。建材方面，ABS管材、ABS卫生洁具、ABS装饰板广泛应用于建材工业。此外ABS还广泛的应用于包装、家具、体育和娱乐用品、机械和仪表工业中。 ABS树脂广泛应用于汽车工业.电器仪表工业和机械工业中,常作齿轮,汽车配件,挡泥板,扶手,冰箱内衬,叶片,轴承,把手,管道,接头,仪表壳,仪表板,盆安全帽等:在家用电器和家用电子设备的应用前景更广阔,如电视机,收录机,冰箱,冷柜,洗衣机,空调机,吸尘器和各种小家电器材:日用品有鞋,包,各种旅游箱,办公设备,玩具及各种容器等,低发泡的ABS能代替木材,适合作建材,家具和家庭用品。