PP SABIC 511A

SABIC® PP 524P is particularly developed for (biaxially) oriented PP film extrusion with a very specific molecular structure providing the ultimate properties required for the stretching process.

Information provided by SABIC

Physical Properties	Metric	English	Comments
Density	0.905 g/cc	0.0327 lb/in3	ASTM D792
Melt Flow	2.00 g/10 min @Load 2.16 kg, Temperature 230 °C	2.00 g/10 min @Load 4.76 lb, Temperature 446 °F	ASTM D1238
Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	102	102	ASTM D785
Tensile Strength, Yield	35.0 MPa	5080 psi	ASTM D638
Film Elongation at Yield, MD	10.0 %	10.0 %	ASTM D638
Flexural Modulus, 1% Secant	1550 MPa	225000 psi	Based on injection molded specimens.; ASTM D790 A
Izod Impact, Notched	0.350 J/cm	0.656 ft-lb/in	ASTM D256

PP SABIC 511A

成型特性

（1）物理性能：PP为无毒、无味的乳白色高结晶的聚合物，是目前所有塑料中最最轻的品种之一，对水特别稳定，在水中14h的吸水率仅为0.01%。分子量约8~15万之间，成型性好。但因收缩率大，原壁制品易凹陷，制品表面光泽好，易于着色。

（2）力学性能：PP的结晶度高，结构规整，因而具有优良的力学性能，其强度和硬度、弹性都比高密度PE(HDPE)高。突出特点是抗弯曲疲劳性（7×10^7）次开闭的折选弯曲而无损坏痕迹，干摩擦系数与尼龙相似，但在油润滑下不如尼龙。

（3）热性能：PP 具有良好的 耐热性，熔点在164~170℃，制品能在100℃以上温度进行消毒灭菌。在不受外力的作用下，150℃也不变形。脆化为-35℃，在低于-35℃会发生脆化。

（4）化学稳定性：PP具有良好的化学稳定性，除能被浓硫酸、浓硝酸侵蚀外，对其他各种化学试剂都比较稳定，但低分子量的脂肪烃、芳香烃等能使PP软化和溶胀，化学稳定性随结晶度的增加还有所提高。所以，PP适合制作俄中化工管道和配件，防腐蚀效果良好。

（5）电性能：聚丙烯的高频绝缘性能优良，由于它几乎不吸水，故绝缘性能不受湿度的影响，有较高的介电系数，且随温度的上升，可以用来制作受热的电气绝缘制品，击穿电压也很高，适用作电器配件等。抗 电压、耐电弧性好，但静电度高，与铜接触易老化。

（6）耐候性：聚丙烯对紫外线很敏感，加入氧化锌硫代丙酸二月桂脂，炭黑式类似的乳白填料等可以改善其耐老化性能。

高透材料

随着人们生活水平不断提高，必然带来在文化、娱乐、食品、医疗、材料、居室装饰等各个方面不同变化的要求与提高，市场中很多物品越来越多地使用透明材料。因此，开发透明PP专用料是一个很好的发展趋势，尤其需要透明性高、流动性好，成型快的PP专用料，以便设计加工成人们喜爱的PP制品。透明PP比普通PP、PVC、PET、PS更具特色，有更多优点和开发前景。

机械及汽车制造零部件

聚丙烯具有良好的机械性能，可以直接制造或改性后制造各种机械设备的零部件，如制造工业管道、农用水管、电机风扇、基建模板等。改性的聚丙烯可模塑成保险杠、防擦条、汽车方向盘、仪表盘及车内装饰件等，大大减轻车身自重达到节约能源的目的。

PP SABIC 511A 可提供COA、COC,ROHS.MSDS.UL黄卡等等资料，价格最优，质量保证！