PC PANLITE G-3430R 

GF 30% reinforced and mold release grade, meeting UL 94 V-2.

Applications:

• Mechanical, electric and electronic components that need mechanical property e.g., stiffness

• Precision machinery components that need dimensional accuracy.

Information provided by Teijin Chemicals Ltd.

Physical Properties	Metric	English	Comments
Density	1.43 g/cc	0.0517 lb/in3	ISO 1183
Moisture Absorption	0.120 % @Temperature 23.0 °C, Time 86400 sec	0.120 % @Temperature 73.4 °F, Time 24.0 hour	ISO 62
Linear Mold Shrinkage, Flow	0.00020 - 0.0020 cm/cm @Thickness 4.00 mm	0.00020 - 0.0020 in/in @Thickness 0.157 in	Teijin method
Linear Mold Shrinkage, Transverse	0.0030 - 0.0050 cm/cm @Thickness 4.00 mm	0.0030 - 0.0050 in/in @Thickness 0.157 in	Teijin method
Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	105 MPa	15200 psi	ISO 527-2/5
Elongation at Break	2.0 %	2.0 %	ISO 527-2/5
Tensile Modulus	8.00 GPa	1160 ksi	ISO 527-2/1
Flexural Strength	160 MPa	23200 psi	2.0 mm/min; ISO 178
Flexural Modulus	7.10 GPa	1030 ksi	2.0 mm/min; ISO 178
Charpy Impact Unnotched	3.50 J/cm2	16.7 ft-lb/in2	ISO 179
Charpy Impact, Notched	1.20 J/cm2	5.71 ft-lb/in2	ISO 179

PC PANLITE G-3430R 

特性:

为非结晶性热塑性塑料，优质的耐热性能、良好的透明度和极高的耐冲击强度等物理机械性能。

优点：

1．具高强度及弹性系数、高冲击强度、使用温度范围广；

2．高度透明性及自由染色性；

3．H.D.T.高；

4．耐疲劳性差；

5、耐候性佳；

6．电气特性优；

7．无味无臭对人体无害符合卫生安全；

8．成形收缩率低、尺寸安定性良好。

应用

PC工程塑料的三大应用领域是玻璃装配业、汽车工业和电子、电器工业，其次还有工业机械零件、光盘、包装、计算机等办公室设备、医疗及保健、薄膜、休闲和防护器材等。PC可用作门窗玻璃，PC层压板广泛用于银行、使馆、拘留所和公共场所的防护窗，用于飞机舱罩，照明设备、工业安全档板和防弹玻璃。

汽车制造业

聚碳酸酯具有良好的抗冲击、抗热畸变性能，而且耐候性好、硬度高，因此适用于生产轿车和轻型卡车的各种零部件，其主要集中在照明系统、仪表板、加热板、除霜器及聚碳酸酯合金制的保险杠等。

建材行业

聚碳酸酯板材具有良好的透光性，抗冲击性，耐紫外线辐射及其制品的尺寸稳定性和良好的成型加工性能，使其比建筑业传统使用的无机玻璃具有明显的技术性能优势。中国建有聚碳酸酯建材中空板生产线20余条，年需用聚碳酸酯7万吨左右，到2005年达到14万吨。

PC PANLITE G-3430R 可提供COA、COC,ROHS.MSDS.UL黄卡等等资料，价格最优，质量保证！