TOPAS 8007X10 is a highly UV-transparent version of our 8007 series of injection molding resins. Like the rest of the 8007 grades, 8007X10 is a glass-clear amorphous polymer with outstanding moisture barrier, chemical resistance, high purity and a non-reactive surface making it an excellent choice for diagnostic and analytical products. It transmits ultraviolet light at lower wavelengths than other polymers. Analytical results are more accurate with pure TOPAS COC and its higher UV transmission for more precise analysis in contact with sensitive chemistries.
Selected Applications
Cuvettes
Microplates
Biochips
Microfluidics
Optics
High purity applications
Healthcare and food contact
Leading Attributes
UV transparency at low wavelengths
Dimensional stability with UV transmission
Purity and chemical resistance
Exceptional mold detail replication; machinable
Clarity, low birefringence, low fluorescence
Not manufactured with BPA, phthalates, or halogens
Broad regulatory compliance
Related Grades for Injection Molding, Healthcare, Optics and Diagnostics
TOPAS 8007S-04 - standard grade, appropriate for most applications
TOPAS 8007D-61 - externally lubricated 8007S-04 for blow molding of bottles, vials, etc.
TOPAS® 8007X10 物性表附加功能
| 基本信息 | |
|---|---|
| 特性 |
|
| 用途 |
|
| 机构评级 |
|
| 外观 |
|
| 形式 |
|
| 加工方法 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 密度 | 1.02 | g/cm3 | ISO 1183 |
| 熔流率（熔体流动速率） (260°C/2.16 kg) | 29 | g/10 min | ISO 1133 |
| 溶化体积流率（MVR） (260°C/2.16 kg) | 32.0 | cm3/10min | ISO 1133 |
| 收缩率 1 | 0.10 到 0.30 | % | 内部方法 |
| 吸水率 (饱和, 23°C) | 0.010 | % | ISO 62 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 拉伸模量 | 2600 | MPa | ISO 527-2/1A/1 |
| 拉伸应力 (屈服) | 63.0 | MPa | ISO 527-2/1A/50 |
| 拉伸应变 (屈服) | 4.5 | % | ISO 527-2/1A/50 |
| 薄膜 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 水气透过率 (23°C, 85% RH) | 0.025 | g·mm/m2/atm/24 hr | DIN 53122 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 简支梁缺口冲击强度 (23°C) | 3.0 | kJ/m2 | ISO 179/1eA |
| 简支梁无缺口冲击强度 (23°C) | 20 | kJ/m2 | ISO 179/1eU |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 热变形温度 (0.45 MPa, 未退火) | 75.0 | °C | ISO 75-2/B |
| 玻璃转化温度 | 78.0 | °C | ISO 11357-2 |
| 维卡软化温度 | 80.0 | °C | ISO 306/B50 |
| 电气性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 体积电阻率 | > 1.0E+16 | ohms·cm | IEC 60093 |
| 相对电容率 | IEC 60250 | ||
| 1 kHz | 2.35 | IEC 60250 | |
| 10 kHz | 2.35 | IEC 60250 | |
| 漏电起痕指数 | > 600 | V | IEC 60112 |
| 可燃性 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| UL 阻燃等级 (1.60 mm) | HB | UL 94 |
| 光学性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 折射率 | 1.530 | ISO 489 | |
| 透射率 | 91.0 | % | ISO 13468-2 |
| 注射 | 额定值 | 单位制 | |
|---|---|---|---|
| 干燥温度 | 50.0 | °C | |
| 干燥时间 | 4.0 到 6.0 | hr | |
| 料筒后部温度 | 190 到 220 | °C | |
| 料筒中部温度 | 200 到 240 | °C | |
| 料筒前部温度 | 220 到 250 | °C | |
| 射嘴温度 | 220 到 250 | °C | |
| 加工（熔体）温度 | 190 到 250 | °C | |
| 模具温度 | 40.0 到 70.0 | °C | |
| 注塑压力 | 50.0 到 110 | MPa | |
| 注射速度 | 中等偏快 | ||
| 保压 | 30.0 到 60.0 | MPa | |
| 背压 | < 15.2 | MPa | |
| 螺杆转速 | 50 到 200 | rpm |