东莞市塑宇化工有限公司
产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 物理性能 | 比重 | ASTM D792 | 1.44-1.46 | |||
| 玻璃纤维含量 | Ash | 20 | % | |||
| 吸水率 | 24hr immersion | ASTM D570 | 0.04 | % | ||
| 成形收缩率 | 流动方向 | - | ASTM D955 | 0.1-0.5 | % | |
| 垂直方向 | - | ASTM D955 | 0.8-1.2 | % | ||
| 机械性能 | 挠曲弹性率 | ASTM D790 | ≥60000 | kg/cm2 | ||
| 挠曲弹性率 | ASTM D790 | ≥60000 | kg/cm2 | |||
| IZOD冲击强度 | 切口1/4″ | ASTM D256 | 5-8 | kg-cm/cm | ||
| 挠曲强度 | ASTM D790 | 1700-2000 | kg/cm2 | |||
| 引张伸长率 | ASTM D638 | 3-5 | % | |||
| 引张强度 | ASTM D638 | 900-1200 | kg/cm2 | |||
| 硬度 | ASTM D785 | 94 | M-Scale | |||
| 电气性能 | 体积抵抗率 | ASTM D257 | ＞1015 | Ω-cm | ||
| 诱电正接 | ASTM D150 | 0.001 | 60Hz | |||
| 耐电弧性 | ASTM D495 | 130 | sec | |||
| 诱电率 | ASTM D150 | 3.4 | 60Hz | |||
| 表面抵抗率 | ASTM D257 | ＞1013 | Ω | |||
| 绝缘破坏强度 | 2mm | ASTM D149 | ＞20 | KV/mm | ||
| 热性能 | 融点 | DSC | 225 | ℃ | ||
| 热变形温度 | 18.6kg/cm2(4.6kg/cm2) | ASTM D648 | 208（220） | ℃ | ||
| 耐燃性 | 0.72mm | UL94 | HB | |||
| 线膨胀系数 | ASTM D696 | 4 | 10-5cm/cm℃ | |||