PA66 THERMOCOMP RF006SXZ 

Physical Properties	Metric	English	Comments
Density	1.40 g/cc	0.0506 lb/in3	ASTM D792
	1.40 g/cc	0.0506 lb/in3	ISO 1183
Moisture Absorption	0.670 %	0.670 %	50% RH, 24 hrs; ASTM D570
	0.990 %	0.990 %	23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow	0.0030 - 0.0050 cm/cm	0.0030 - 0.0050 in/in	24 hrs; ASTM D955
Linear Mold Shrinkage, Transverse	0.0090 - 0.020 cm/cm	0.0090 - 0.020 in/in	24 hrs; ASTM D955
Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	194 MPa	28100 psi	5 mm/min; ISO 527
	200 MPa	29000 psi	Type I, 5 mm/min; ASTM D638
Tensile Strength, Yield	195 MPa	28300 psi	5 mm/min; ISO 527
	200 MPa	29000 psi	Type I, 5 mm/min; ASTM D638
Elongation at Break	3.3 %	3.3 %	Type I, 5 mm/min; ASTM D638
	3.4 %	3.4 %	5 mm/min; ISO 527
Elongation at Yield	3.3 %	3.3 %	5 mm/min; ISO 527
	3.3 %	3.3 %	Type I, 5 mm/min; ASTM D638
Flexural Strength	279 MPa	40500 psi	ISO 178
	286 MPa	41500 psi	1.3 mm/min, 50 mm span; ASTM D790
Flexural Yield Strength	286 MPa	41500 psi	1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus	9.25 GPa	1340 ksi	2 mm/min; ISO 178
	9.51 GPa	1380 ksi	1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched	1.34 J/cm	2.51 ft-lb/in	ASTM D256
Izod Impact, Unnotched	12.8 J/cm	24.0 ft-lb/in	ASTM D4812
Izod Impact, Notched (ISO)	14.0 kJ/m2	6.66 ft-lb/in2	80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO)	82.0 kJ/m2	39.0 ft-lb/in2	80*10*4; ISO 180/1U

PA66 THERMOCOMP RF006SXZ 

PA66特性

1、具有优良的耐磨性、自润滑性，机械强度较高。但吸水性较大，因而尺寸稳定性较差

2、PA66在较高温度也能保持较强的强度和刚度。PA66在成型后仍然具有吸湿性，其程度主要取决于材料的组成、壁厚以及环境条件。

3、在产品设计时，一定要考虑吸湿性对几何稳定性的影响。为了提高PA66的机械特性，经常加入各种各样的改性剂。玻璃就是最常见的添加剂，有时为了提高抗冲击性还加入合成橡胶，如EPDM和SBR等。PA66的粘性较低，因此流动性很好（但不如PA6）。这个性质可以用来加工很薄的元件。它的粘度对温度变化很敏感。

4、PA66的收缩率在1%~2%之间，加入玻璃纤维添加剂可以将收缩率降低到0.2%~1% 。收缩率在流程方向和与流程方向相垂直方向上的相异是较大的。PA66对许多溶剂具有抗溶性，但对酸和其它一些氯化剂的抵抗力较弱。

PA66应用

高温电气插座零件、电气零件、齿轮、轴承、滚子、弹簧支架、滑轮、螺栓、叶轮、风扇叶片、螺旋桨、高压封口垫片、阀座、输油管、储油容器、绳索、扎带、传动皮带、砂轮粘合剂、电池箱、绝缘电气零件、线芯、抽丝等

PA66 THERMOCOMP RF006SXZ 可提供COA、COC,ROHS.MSDS.UL黄卡等等资料，价格最优，质量保证！