东莞市塑宇化工有限公司
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 物理性能 | 填充含量 | 30 | Wt% | |||
| 比重 | ASTM D792 | 1.52 | ||||
| 吸水率 | 23℃,24hr | ASTM D570 | 0.07 | % | ||
| 成型收缩率 | - | 平行方向 | 0.2 | % | ||
| - | 垂直方向 | 0.7 | % | |||
| 机械性能 | 拉伸强度 | ASTM D638 | 132.4 | MPa | ||
| 拉伸长度 | ASTM D638 | 4 | % | |||
| 弯曲强度 | ASTM D790 | 196.1 | MPa | |||
| 弯曲模量 | ASTM D790 | 7.85 | Gpa | |||
| Izod缺口冲击强度 | 3.2mm | ASTM D256 | 98 | J/M | ||
| 洛氏硬度 | ASTM D785 | 120 | R | |||
| 摩擦系数 | ASTM D1894 | 0.15 | ||||
| 电气性能 | 介电常数 | 106Hz | ASTM D150 | 30 | pF/m | |
| 介电损耗正切值 | 106Hz | ASTM D150 | 0.016 | |||
| 体积电阻系数 | ASTM D257 | 1016 | ||||
| 耐电压 | ASTM D149 | 25 | KV/mm | |||
| 电弧电阻系数 | ASTM D495 | 130 | S | |||
| 热性能 | 熔点 | DSC法 | 224 | ℃ | ||
| 负荷挠曲温度 | - | 0.45MPa | ASTM D648 | 220 | ℃ | |
| - | 1.86Mpa | ASTM D648 | 215 | ℃ | ||
| 线膨胀系数 | 3.0 | |||||
| 阻燃性 | UL94 | HB | ||||
| 比热 | 0.5 | |||||