东莞市常平山鑫塑胶原料经营部
东莞市山鑫(国际）塑胶有限公司长期供应如下型号产品：我司可随货提供UL黄卡 SGS SMDS等相关资料 欢迎新老客户来电咨询！、
LEXAN ML3982 PC
LEXAN ML3987 PC
LEXAN ML3999 PC
LEXAN ML4248 PC
LEXAN ML4249 PC
LEXAN ML4351 PC
LEXAN ML4506 PC
LEXAN ML4539 PC
LEXAN ML4588 PC
LEXAN ML5221 PC
LEXAN ML5472 PC
LEXAN ML6018R PC
LEXAN ML6031 PC
LEXAN ML6076 PC
LEXAN ML6230 PC
LEXAN ML6240 PC
LEXAN ML6411 PC
LEXAN ML6412 PC
LEXAN ML6413 PC
LEXAN ML6430 PC
LEXAN ML6451 PC
LEXAN ML6739 PC
LEXAN ML6819 PC
LEXAN ML7647 PC
LEXAN ML7647K PC
LEXAN ML7652 PC
LEXAN ML7664 PC
LEXAN ML7666 PC
LEXAN ML7667 PC
LEXAN ML7672 PC
LEXAN ML7677 PC
LEXAN ML7678 PC
LEXAN ML7681 PC
LEXAN ML7682 PC
LEXAN ML7686 PC
LEXAN ML7686E PC
LEXAN ML7687 PC
LEXAN ML7691 PC
LEXAN OQ1022 PC
LEXAN OQ1022 PC
LEXAN OQ1022 PC
LEXAN OQ1023 PC
LEXAN OQ1026 PC
LEXAN OQ1028 PC
LEXAN OQ1060 PC
LEXAN OQ2320 PC
LEXAN OQ2720 PC
SABIC Innovative Plastics Lexan® ML3982 PC (Europe-Africa-Middle East) 物性表
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | 1.20 g/cc | 0.0434 lb/in3 | ISO 1183 |
| 水分吸收 | 0.150 % | 0.150 % | 23°C / 50% RH; ISO 62 |
| 饱和吸水率 | 0.35 % | 0.35 % | ISO 62 |
| 线性成型收缩率,Flow | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | on Tensile Bar; SABIC Method |
| Melt Index of Compound | 6.0 g/10 min @Load 1.20 kg, Temperature 250 °C |
6.0 g/10 min @Load 2.65 lb, Temperature 482 °F |
MVR [cm^3/10 min]; ISO 1133 |
| 40 g/10 min @Load 1.20 kg, Temperature 300 °C |
40 g/10 min @Load 2.65 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 硬度，H358/30 | 95.0 MPa | 13800 psi | ISO 2039-1 |
| 抗张强度(断裂) | 55.0 MPa | 7980 psi | 50 mm/min; ISO 527 |
| 抗张强度(屈服) | 60.0 MPa | 8700 psi | 50 mm/min; ISO 527 |
| 伸长率 (断裂) | 70 % | 70 % | 50 mm/min; ISO 527 |
| 屈服伸长率 | 6.0 % | 6.0 % | 50 mm/min; ISO 527 |
| 拉伸模量 | 2.30 GPa | 334 ksi | 1 mm/min; ISO 527 |
| 弯曲强度 | 85.0 MPa | 12300 psi | 2 mm/min; ISO 178 |
| 弯曲模量 | 2.30 GPa | 334 ksi | 2 mm/min; ISO 178 |
| 泰伯磨损，毫克/1000次 | 10 | 10 | CS-17, 1 kg; SABIC Method |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 体积电阻率 | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 |
| 表面电阻 | >= 1.00e+15 ohm | >= 1.00e+15 ohm | ROA; IEC 60093 |
| 介电常数 | 2.7 @Frequency 1.00e+6 Hz |
2.7 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 2.7 @Frequency 50.0 - 60.0 Hz |
2.7 @Frequency 50.0 - 60.0 Hz |
IEC 60250 | |
| 介电强度 | 17.0 kV/mm @Thickness 3.20 mm |
432 kV/in @Thickness 0.126 in |
in oil; IEC 60243-1 |
| 27.0 kV/mm @Thickness 1.60 mm |
686 kV/in @Thickness 0.0630 in |
in oil; IEC 60243-1 | |
| 35.0 kV/mm @Thickness 0.800 mm |
889 kV/in @Thickness 0.0315 in |
in oil; IEC 60243-1 | |
| 耗散因数 | 0.0010 @Frequency 50.0 - 60.0 Hz |
0.0010 @Frequency 50.0 - 60.0 Hz |
IEC 60250 |
| 0.010 @Frequency 1.00e+6 Hz |
0.010 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线形热膨胀系数 - 流动 | 70.0 μm/m-°C @Temperature 23.0 - 80.0 °C |
38.9 μin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 |
| 导热系数 | 0.200 W/m-K | 1.39 BTU-in/hr-ft2-°F | ISO 8302 |
| 载荷下热变形温度(0.46 MPa) | 130 °C | 266 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 133 °C | 271 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be | |
| 载荷下热变形温度(1.8 MPa) | 120 °C | 248 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 121 °C | 250 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae | |
| 维卡软化温度 | 139 °C | 282 °F | Rate B/50; ISO 306 |
| 140 °C | 284 °F | Rate B/120; ISO 306 | |
| 145 °C | 293 °F | Rate A/50; ISO 306 | |
| 可燃性(UL94) | V-2 @Thickness 0.750 mm |
V-2 @Thickness 0.0295 in |
UL 94 by SABIC-IP |
| 极限氧指数 | 25 % | 25 % | ISO 4589 |
| 灼热丝试验 | 850 °C @Thickness 1.00 mm |
1560 °F @Thickness 0.0394 in |
IEC 60695-2-12 |
| 光学性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 折射率 | 1.586 | 1.586 | ISO 489 |
| 雾度 | <= 0.80 % @Thickness 2.54 mm |
<= 0.80 % @Thickness 0.100 in |
ASTM D1003 |
| Transmission, Visible | 88 - 90 % | 88 - 90 % | 2.54 mm; ASTM D1003 |
| 材料描述 | 测试方法 | |
|---|---|---|
| 球压试验，125°C+/-2℃ | PASSES | IEC 60695-10-2 |
PC 聚碳酸酯
典型应用范围:
电气和商业设备（计算机元件、连接器等），器具（食品加工机、电冰箱抽屉等），交通运输行业（车辆的前后灯、仪表板等）。
化学和物理特性:
PC是一种非晶体工程材料，具有特别好的抗冲击强度、热稳定性、光泽度、抑制细菌特性、阻燃特性以及抗污染性。PC的缺口伊估德冲击强度（otched Izod impact stregth）非常高，并且收缩率很低，一般为0.1%~0.2%。PC有很好的机械特性，但流动特性较差，因此这种材料的注塑过程较困难。在选用何种品质的 PC材料时，要以产品的最终期望为基准。如果塑件要求有较高的抗冲击性，那么就使用低流动率的PC材料；反之，可以使用高流动率的PC材料.
山鑫（国际）塑胶贸易公司诚信经营，重信用、守合同，保证产品质量，以多品种经营特色和薄利多销的原则，赢得了广大客户的信任！
主营系列:POM；PPO；PA6；PA66；PC；PP；ABS:PBT；ASA;AES;;PC/ABS;TPX
PA/ABS;POE;ABS高胶粉; ABS；AS；GPPS；HIPS；LDPE；LLDPE；PCTG;
HDPE；PA46；PA6T；PA9T,PA12；PMMA；MS；EVOH,POE,PC/AES;PBT/ABS;PETG;PCTA;
PPS；PBT；LCP；TPE；TPU；PEEK；K{Q}胶：日本合成化学EVOH新料副牌等。
可提供原厂物理性能表，UL黄卡，COC，SGS等资料！本公司诚信经营，重信用、守合同，保证产品质量。欢迎来电咨询洽谈！
批发说明本公司支持提倡各种优惠活动，多买多优惠，薄利多销为原则，赢得广大的口碑
★ 客户拿一包试模打样，按批发价供给，祝客户试摸成功
★ 客户试摸成功，订购低于1吨按低于当天市场价格优惠供给
★ 客户订货1吨以上免费可送货上门;，按批发价格供给，长期合作。
★ 东莞浩云塑胶，欢迎你选购！
运费说明：支持物流，快递和货运; 支持现金，银行转账.
★ 本公司原料低于1吨，不承担运费，订货1吨以上广东地区可送货上门; 省外客户物流，快递或货运; 不便之处敬请谅解，谢谢!
★ 选用物流或者快递的买家，请先确认当地是否有该物流或快递的营业网点。
★ 原料到厂后，请不要拆外包装，应先仔细检查原料的外包装是否完好及原料型号是否与您所订购原料型号相匹配。
★ 货物送达后，请第一时间检查，发现物流过程中出现大量包装损坏及原料外漏的,请让物流人员出具证明并保存，并在24小时内与我们联系。
★ 如发货后未能及时收到，请及时与我们联系。
★ 本公司原料售后的注塑加工由客户负责，如需帮助，我公司工程部将竭尽所能与您共同协商处理。
★ 本公司随货的基本资料包括《送货单》两联、《货款收据》一张、《商务经理名片》一张
注：25公斤/包起订,批量可折扣,款到发货或物流代收款. 珠三角一天内到达,国内各地五天内到货.
温馨提示：因塑料行情每天都会有变更，页面上有些报价可能会与当天实际报价有所差异，仅供参考！ 若需要材料详细物性资料及环保证书等，请电邮：tzplas@163.com索取。感谢您的配合与支持!
1吨以上在广东省以内可以免费送货上门 ...详细请咨询 18926874899罗生