LNP THERMOCOMP UF008AS is a compound based on Polyphthalamide resin, containing Glass Fiber. Added features include; Mold Release. Information provided by SABIC

PPA THERMOCOMP UF008AS 

Physical Properties	Metric	English	Comments
Density	1.53 g/cc	0.0553 lb/in3	ISO 1183
Linear Mold Shrinkage, Flow	0.0014 cm/cm	0.0014 in/in	SABIC method
Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	234 MPa	33900 psi	5 mm/min; ISO 527
Elongation at Break	2.1 %	2.1 %	5 mm/min; ISO 527
Flexural Yield Strength	315 MPa	45700 psi	2 mm/min; ISO 178
Flexural Modulus	12.0 GPa	1740 ksi	2 mm/min; ISO 178
Izod Impact, Notched (ISO)	13.0 kJ/m2	6.19 ft-lb/in2	80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO)	55.0 kJ/m2	26.2 ft-lb/in2	80*10*4; ISO 180/1U
Tangent Modulus	14500 MPa	2.10e 6 psi	1 mm/min; ISO 527

PPA THERMOCOMP UF008AS 

特性

PPA强度、韧度和硬度优越性能，以及其良好的耐热件，耐化学性及抗开裂能力

PPA由于高温和高湿环境下仍能保持强度和硬度，可在传统的尼龙和聚酯所无法随的就用中替换金属

PPA塑料还具有优越的表面光泽性。可以对其进行着色而避免了表面喷涂，从而有助于降低表面划痕和刮痕的明显程度。

PPA塑料还具有良好的可加工性，并允许短的注塑循环时间

与PA46相比:

PPA具有比PA46更高的热稳定性；

PPA具有比PA46更好的CTI/耐电弧能和红外同流能力；

PPA具有比PA46更好的耐化学性；

应用

 汽车部件，包括燃油、传动及发动机系统，可减轻重量、降低成本并提供长时间的使用寿命；

 芯片组和插座、杯体焊接支座；

 片状电容器、开关及微型喇叭、制作高密度的印刷电路板连接器；

 用于耐磨要求极高的场合，例如无润滑轴承、密封、轴承隔离环和往复开压缩机零件；

 连接器、控制器、传感器、马达及其它关键电子部件

PPA THERMOCOMP UF008AS 可提供COA、COC,ROHS.MSDS.UL黄卡等等资料，价格最优，质量保证！