40% Long glass fiber reinforced, heat stabilized, Nylon 6/6

Information provided by Celanese

CELSTRAN PA66-GF40-02-US

Physical Properties	Metric	English	Comments
Specific Gravity	1.45 g/cc	1.45 g/cc	ASTM D792
Density	1.45 g/cc	0.0524 lb/in3	ISO 1183
Linear Mold Shrinkage, Flow	0.0010 - 0.0020 cm/cm	0.0010 - 0.0020 in/in	ASTM D955
Linear Mold Shrinkage, Transverse	0.0020 - 0.0030 cm/cm	0.0020 - 0.0030 in/in	ASTM D955
Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	215 MPa	31200 psi	5mm/min; ISO 527-2/1A
	253 MPa	36700 psi	ASTM D638
	134 MPa @Temperature 121 °C	19400 psi @Temperature 250 °F	ASTM D638
	270 MPa @Temperature -40.0 °C	39100 psi @Temperature -40.0 °F	ASTM D638
Tensile Strength	120 MPa @Temperature 80.0 °C	17400 psi @Temperature 176 °F	ISO 527-1, -2
Elongation at Break	2.0 %	2.0 %	5mm/min; ISO 527-2/1A
	2.3 %	2.3 %	ASTM D638
	2.2 % @Temperature 4.44 °C	2.2 % @Temperature 40.0 °F	ASTM D638
	2.5 % @Temperature 121 °C	2.5 % @Temperature 250 °F	ASTM D638
	2.9 % @Temperature 80.0 °C	2.9 % @Temperature 176 °F	ISO 527-1, -2

CELSTRAN PA66-GF40-02-US

PA66特性

1、具有优良的耐磨性、自润滑性，机械强度较高。但吸水性较大，因而尺寸稳定性较差

2、PA66在较高温度也能保持较强的强度和刚度。PA66在成型后仍然具有吸湿性，其程度主要取决于材料的组成、壁厚以及环境条件。

3、在产品设计时，一定要考虑吸湿性对几何稳定性的影响。为了提高PA66的机械特性，经常加入各种各样的改性剂。玻璃就是最常见的添加剂，有时为了提高抗冲击性还加入合成橡胶，如EPDM和SBR等。PA66的粘性较低，因此流动性很好（但不如PA6）。这个性质可以用来加工很薄的元件。它的粘度对温度变化很敏感。

4、PA66的收缩率在1%~2%之间，加入玻璃纤维添加剂可以将收缩率降低到0.2%~1% 。收缩率在流程方向和与流程方向相垂直方向上的相异是较大的。PA66对许多溶剂具有抗溶性，但对酸和其它一些氯化剂的抵抗力较弱。