POM CELCON UV270Z 

Physical Properties	Metric	English	Comments
Specific Gravity	1.41 g/cc	1.41 g/cc	ASTM D792
Density	1.41 g/cc	0.0509 lb/in3	ISO 1183
Moisture Absorption	0.200 %	0.200 %	23°C/50%RH; ISO 62
Water Absorption at Saturation	0.75 %	0.75 %	ISO 62
Linear Mold Shrinkage, Flow	0.017 cm/cm	0.017 in/in	ISO 294-4
	0.022 cm/cm	0.022 in/in	ASTM D955
Linear Mold Shrinkage, Transverse	0.016 cm/cm	0.016 in/in	ISO 294-4
	0.018 cm/cm	0.018 in/in	ASTM D955
Melt Flow	27 g/10 min	27 g/10 min	ASTM D1238
	23 g/10 min @Load 2.16 kg, Temperature 190 °C	23 g/10 min @Load 4.76 lb, Temperature 374 °F	[cm3/10min]; ISO 1133
Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	60.7 MPa	8800 psi	ASTM D638
	64.0 MPa	9280 psi	50mm/min; ISO 527-2/1A
Elongation at Yield	8.0 %	8.0 %	50mm/min; ISO 527-2/1A
Tensile Modulus	2.70 GPa	392 ksi	50mm/min; ISO 527-2/1A
Flexural Modulus	2.59 GPa	375 ksi	ASTM D790
	2.76 GPa	400 ksi	ISO 178
Izod Impact, Notched	0.534 J/cm	1.00 ft-lb/in	ASTM D256
Izod Impact, Notched (ISO)	5.10 kJ/m2	2.43 ft-lb/in2	ISO 180/1A
Charpy Impact, Notched	0.470 J/cm2	2.24 ft-lb/in2	ISO 179/1eA

POM CELCON UV270Z 

改性POM

⒈增强POM

主要增强材料为玻璃纤维、玻璃球或碳纤维等，并且玻璃纤维最常用，增强后的力学性能可提高2～3倍，热变形温度提高50℃以上。

⒉高润滑POM

在POM中加入石墨、F4、二硫化钼、润滑油及低分子量PE等，可提高其润滑性能。例如，在POM中加入5份F4，可降低摩擦因数60%，耐磨性提高1～2倍。再如，在POM中加入液体润滑油，可大幅度提高耐磨性和极限PV值。为提高由油的分散效果，需加入炭黑、氢氧化铝硫酸钡、乙丙橡胶等吸油载体。加入5%油POM的摩擦性提高72%，极限PV值可达3.9MPa·m/s（纯POM为0.213MPa·m/s），为其他工程塑料的3～20倍。

（1）POM是结晶型塑料,密度为1.42g/cm3,它的钢性很好,俗称“赛钢”.

　　（2）它具有耐疲劳、耐蠕变、耐磨、耐热、耐冲击等优良的性能,且摩擦系数小,自润滑性好.

　　（3）POM不易吸湿,吸水率为0.22～0.25%,在潮湿的环境中尺寸稳定性好,其收缩率为2.1%(较大),注塑时尺寸较难控制,热变形温度为172℃,聚甲醛有均聚甲醛两种,性能不同(均聚甲醛耐温性好一点).