LDPE SABIC 2100N0W
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 0.921 g/cc | 0.0333 lb/in3 | ASTM D1505 |
Melt Flow | 0.33 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.33 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
Mechanical Properties | Metric | English | Comments |
Film Tensile Strength at Yield, TD | 11.0 MPa | 1600 psi | ISO 527-3 |
Film Elongation at Break, MD | >= 200 % | >= 200 % | ISO 527-3 |
Film Elongation at Break, TD | >= 500 % | >= 500 % | ISO 527-3 |
Tensile Modulus | 0.190 GPa | 27.6 ksi | TD; ISO 527-3 |
Coefficient of Friction | 1.0 | 1.0 | ASTM D1894 |
Tear Strength | 30.0 kN/m | 171 pli | TD; ISO 6383-2 |
Dart Drop Total Energy | 300 J/cm | 0.562 ft-lb/mil | ASTM D4272 |
Film Tensile Strength at Break, MD | 28.0 MPa | 4060 psi | ISO 527-3 |
Film Tensile Strength at Break, TD | 23.0 MPa | 3340 psi | ISO 527-3 |
LDPE SABIC 2100N0W
(1)乙烯聚合反应过程是一个强烈的放热过程。乙烯的聚合热约为93.5kJ/mol(或3.3kJ/g),在235MPa、150~300℃下乙烯的比热容为2.51~2.85J/(g·℃),反应热如果不能及时移去,每1%乙烯发生聚合将使温度升高12~13℃。如果温度过高,还会导致乙烯分解。
(2)在高压下,乙烯已被压缩到密度为0.5g/mL的气密相状态,近似于不能再压缩的液体,此时乙烯分子间的距离显著缩短,从而增加了游离基与乙烯分子的碰撞概率,所以容易发生聚合反应。
(3)高温下增长链的自由基活性大,容易发生链转移反应,所得到的聚合物为带有较多支链的线型结构。通常每1000个碳链原子中含有20~30个支链,结晶度为45%~65%,密度在0.910~0.925g/mL,质轻、具柔性,耐低温性、耐冲击性较好。
LDPE产品性能
低密度聚乙烯其特征主要有以下几点:
(1)薄膜呈微乳白透明色,柔软。强度比高密度聚乙烯小,抗冲击强度则比高密度聚乙烯大。
(2)耐寒、耐低温及耐较高温度。较厚的薄膜能承受90℃热水浸泡的杀菌过程。
(3)防潮性能比较好,化学性能稳定,不溶于一般溶剂。
(4)有较大的透气性,故用作易氧化的食品包装时,其内容物的贮存期不宜过长。
(5)耐油脂性较差,制品能被缓慢溶涨。包装含油脂食品时,久贮后会使食品出现哈喇味。
(6)长时期受紫外线及热作用会老化,影响其物理性能和介电性能。
(7)熔点为110~115℃,加工温度为150~210℃,若在惰性气体中,温度可达300℃仍稳定。但熔体和氧接触易发生降解作用。
LDPE应用领域
低密度聚乙烯的应用范围:适用于调味料、糕点、糖、蜜饯、饼干、奶粉、茶叶、鱼肉松等食品包装。片剂、粉剂等药品包装,衬衫、服装、针织棉制品及化纤制品等纤维制品包装。洗衣粉、洗涤剂、化妆品等日化用品包装。由于单层PE薄膜的机械性能较差,所以通常用作复合包装袋的内层,即多层复合薄膜热封性基材。