东莞市恒磊塑胶有限公司
ABS THERMOCOMP AF004XXY
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.19 g/cc | 1.19 g/cc | ASTM D792 |
| Density | 1.19 g/cc | 0.0430 lb/in3 | ISO 1183 |
| Moisture Absorption | 0.250 % | 0.250 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm | 0.0020 in/in | 24 hrs; ASTM D955 |
| 0.0020 cm/cm | 0.0020 in/in | 24 hrs; ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0040 cm/cm | 0.0040 in/in | 24 hrs; ASTM D955 |
| 0.0040 cm/cm | 0.0040 in/in | 24 hrs; ISO 294 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 76.0 MPa | 11000 psi | Type I, 5 mm/min; ASTM D638 |
| 77.0 MPa | 11200 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 1.8 % | 1.8 % | 5 mm/min; ISO 527 |
| 2.0 % | 2.0 % | Type I, 5 mm/min; ASTM D638 | |
| Flexural Strength | 119 MPa | 17300 psi | ISO 178 |
| 122 MPa | 17700 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 5.97 GPa | 866 ksi | 2 mm/min; ISO 178 |
| 6.08 GPa | 882 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.800 J/cm | 1.50 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.74 J/cm | 7.01 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m2 | 3.33 ft-lb/in2 | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 23.0 kJ/m2 | 10.9 ft-lb/in2 | 80*10*4; ISO 180/1U |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Instrumented Impact Total Energy | 13.0 J | 9.59 ft-lb | ASTM D3763 |
| Tangent Modulus | 6040 MPa | 876000 psi | 1 mm/min; ISO 527 |
| 6080 MPa | 882000 psi | 50 mm/min; ASTM D638 | |
ABS THERMOCOMP AF004XXY
成型性能
无定形材料,流动性中等,吸湿大,必须充分干燥,表面要求光泽的塑件须长时间预热干燥80-90度,3小时；
宜取高料温,高模温,但料温过高易分解(分解温度为>270度).对精度较高的塑件,模温宜取50-60度,对高光泽.耐热塑件,模温宜取60-80度；
如需解决夹水纹，需提高材料的流动性，采取高料温、高模温，或者改变入水位等方法；
如成形耐热级或阻燃级材料，生产3-7天后模具表面会残存塑料分解物，导致模具表面发亮，需对模具及时进行清理，同时模具表面需增加排气位置；
冷却速度快，模具浇注系统应以粗，短为原则，宜设冷料穴，浇口宜取大，如：直接浇口，圆盘浇口或扇形浇口等，但应防止内应力增大，必要时可采用调整式浇口。模具宜加热，应选用耐磨钢；
料温对塑件质量影响较大，料温过低会造成缺料，表面无光泽，银丝紊乱料温过高易溢边，出现银丝暗条，塑件变色起泡；
用途
ABS树脂的最大应用领域是汽车、电子电器和建材。汽车领域的使用包括汽车仪表板、车身外板、内装饰板、方向盘、隔音板、门锁、保险杠、通风管等很多部件。在电器方面则广泛应用于电冰箱、电视机、洗衣机、空调器、计算机、复印机等电子电器中。建材方面，ABS管材、ABS卫生洁具、ABS装饰板广泛应用于建材工业。此外ABS还广泛的应用于包装、家具、体育和娱乐用品、机械和仪表工业中。