EVA ELVAX 3165SB

Physical Properties	Metric	English	Comments
Density	0.940 g/cc	0.0340 lb/in3	ASTM D792
Moisture Vapor Transmission	1.42 cc-mm/m2-24hr-atm @Thickness 0.0254 mm	3.61 cc-mil/100 in2-24hr-atm @Thickness 0.00100 in	g-mm/m2-day; based on film thickness; ASTM E96; ASTM E96
Oxygen Transmission	264 cc-mm/m2-24hr-atm @Thickness 0.0254 mm	671 cc-mil/100 in2-24hr-atm @Thickness 0.00100 in	film; ASTM D3985
Melt Flow	0.70 g/10 min	0.70 g/10 min	Condition not noted.; ASTM D1238
Mechanical Properties	Metric	English	Comments
Film Elongation at Break, MD	530 %	530 %	MD-TD Average; ASTM D882
Film Elongation at Break, TD	530 %	530 %	MD-TD Average; ASTM D882
Impact	31.6	31.6	J/mm Spencer Impact; Average of MD and TD; ASTM D3420
Elmendorf Tear Strength, MD	4.17 g/micron	106 g/mil	Average of MD and TD; ASTM D1922
Film Tensile Strength at Break, MD	31.0 MPa	4500 psi	MD-TD Average; ASTM D882
Thermal Properties	Metric	English	Comments
Melting Point	68.0 °C	154 °F	Freezing Point via DSC/ASTM D3418
	88.0 °C	190 °F	Freezing Point via DSC/ASTM D3418

EVA ELVAX 3165SB

特性

是是广泛用于发泡鞋材、功能性棚膜、包装模、热熔胶、电线电缆及玩具等领域。

1、乙酸乙烯含量在5%以下的EVA，其主要产品是薄膜、电线电缆、LDPE改性剂、胶粘剂等；

2、乙酸乙烯含量在5%~10% 的EVA产品为弹性薄膜等；

3、乙酸乙烯含量在20~28%的EVA，主要用于热熔粘合剂和涂层制品；

EVA是由LLDPE（线性低密度聚乙烯）和醋酸（VA）共聚而成。

EVA的聚合方法：

1、高压本体聚合 （塑料制品）

2、溶液聚合 （PVC加工助剂）

3、乳液聚合 （粘合剂制品）

4、悬浮聚合

乙酸乙烯（VA）含量高于30%的采用乳液聚合；

乙酸乙烯（VA）含量低的就采用高压本体聚合。

影响EVA性能的主要因素：

1、Melt Index 熔融指数（简称MI,溶指）

2、VA% 醋酸的含量

熔融指数（MI）一定，乙酸乙烯（VA)含量越高，其弹性、柔软性、相溶性、透明性等也越高；当VA的含量减少的时候，它的性能接近于聚乙烯（PE），刚性增高，耐磨性、电绝缘性提高。

应用

1、广泛用于发泡鞋材、功能性棚膜、包装模、热熔胶、电线电缆及玩具等领域。

2、乙酸乙烯含量在5%~10% 的EVA产品为弹性薄膜等；

3、乙酸乙烯含量在20~28%的EVA，主要用于热熔粘合剂和涂层制品；

4、乙酸乙烯含量在5%~45%，主要产品为薄膜（包括农用薄膜）和片材，注塑、模塑制品，发泡制品，热熔粘合剂等。