PPS FORTRON 6850L6 

Physical Properties	Metric	English	Comments
Specific Gravity	1.80 g/cc	1.80 g/cc	ASTM D792
Density	1.80 g/cc	0.0650 lb/in3	ISO 1183
Water Absorption	0.020 % @Temperature 22.8 °C	0.020 % @Temperature 73.0 °F	24hr immersion; ASTM D570
Water Absorption at Saturation	0.020 %	0.020 %	ISO 62
Linear Mold Shrinkage, Flow	0.0020 - 0.0040 cm/cm	0.0020 - 0.0040 in/in	ASTM D955
	0.0030 - 0.0060 cm/cm	0.0030 - 0.0060 in/in	ISO 294-4
Linear Mold Shrinkage, Transverse	0.0030 - 0.0050 cm/cm	0.0030 - 0.0050 in/in	ASTM D955
	0.0040 - 0.0060 cm/cm	0.0040 - 0.0060 in/in	ISO 294-4
Mechanical Properties	Metric	English	Comments
Hardness, Rockwell M	96	96	ISO 2039-2
	96	96	ASTM D785
Tensile Strength at Break	124 MPa	18000 psi	ASTM D638
	125 MPa	18100 psi	5mm/min; ISO 527-2/1A
Elongation at Break	1.0 %	1.0 %	5mm/min; ISO 527-2/1A
	1.0 %	1.0 %	ASTM D638
Tensile Modulus	18.5 GPa	2680 ksi	50mm/min; ISO 527-2/1A
Flexural Strength	190 MPa	27600 psi	ISO 178
	193 MPa	28000 psi	ASTM D790

PPS FORTRON 6850L6 主要用途

pps的应用是以其优异的耐热性为中心，兼顾它的减摩自润滑性，化学稳定性、尺寸稳定性，阻燃性和电绝缘性等。在化工行业pps可用作合成、输送、储存物料的反应罐、管道、阀门、化工泵等，在机械中心pps可制作叶轮、叶片、齿轮、偏心轮、轴承、离合器及耐磨零件；pps的主要用途还是在电子电器领域，如制作变压器骨架，高频线圈骨架、插头、插座、接线架、接触器转鼓鼓片及各种精密零件等。

PPS FORTRON 6850L6 特性

（1）一般性能：PPS为一种外观白色、高结晶度、硬而脆的聚合物，纯PPS的相对密度为1.3，但改性后会增大。PPS有吸水率极小，一般只有0.03%左右。

（2）机械性能：纯PPS的机械性能不高，尤其冲击强度比较低。以玻璃纤维增强后会大幅度提高冲击强度，由27J/m增大到76J/m，增大3倍；拉伸强度由6Mpa增大到137Mpa，增大1倍。PPS的刚性很高，在工程塑料中少见。纯PPS的弯曲模量可达3.8Gpa，无机填充改性后可达到12.6Gpa,增大5倍之多。

（3）热学性能：PPS具有优异的热性能，短期可耐260℃，并可在200~240℃下长期使用；其耐热性与PI相当，仅次于F4塑料，这在热固性塑料中也不多见。

（4）电学性能：PPS的电性能十分突出，与其他工程塑料相比，其介电常数和介电损耗角正切值都比较低，并且在较大的频率、温度及温度范围内变化不大；PPS的耐电弧好，可与热固性塑料媲美。PPS常用于电器绝缘材料，其用量可占30%左右。

（5）耐化学性能：PPS的最大特点之一为耐化学腐蚀性好，其化学稳定性能仅次于F4；PPS对大多酸、酯、酮、醛、酚及脂肪烃、芳香烃、氯代烃等稳定，不耐氯代联苯及氧化性酸、氧化剂、浓硫酸、浓硝酸、王水、过氧化氢及次氯酸钠等。PPS的耐辐射性好。

（6）PPS的阻燃性好，其氧指数高达44%以上；与其他塑料相比，它在塑料中属于高阻燃材料（纯PVC的氧指数为47%、PSF为30%、PA66为29%、MPPO为28%，PC为25%）。