Glass Reinforced Resins
玻璃纤维增强树脂
《电脑端可查看产品物性》
Zytel® 70G35HSL NC010 is a 35% glass fiber reinforced, heat stabilized polyamide 66 resin for injection molding.
zytel®70G35HSL NC010是一个35%玻璃纤维增强，热稳定聚酰胺66树脂注塑成型。
Property |
Test Method |
Units |
Value |
|
DAM |
50%RH |
|||
Identification Resin Identification Part Marking Code |
ISO 1043 ISO 11469 |
PA66-GF35 >PA66-GF35< |
||
Mechanical Stress at Break Strain at Break Tensile Modulus Notched Charpy Impact Strength -30℃(-22℉) 23℃(73℉) Unnotched Charpy Impact Strength -30℃(-22℉) 23℃(73℉) |
ISO 527 ISO 527 ISO 527 ISO 179/1eA ISO 179/1eU |
MPa(kpsi) % MPa(kpsi) 2 kJ/m 2 kJ/m |
210(30.5) 3.2 11200(1600) 10 15 80 90 |
145(21.0) 4.6 8300(1200) 10 18 75 100 |
Thermal Deflection Temperature 0.45MPa 1.80MPa Melting Temperature 10℃/min |
ISO 75f ISO 11357-1/-3 |
℃(℉) ℃(℉) |
261(502) 252(486) 262(504) |
|
Property |
Test Method |
Units |
Value |
|
DAM |
50%RH |
|||
Thermal CLTE, Normal 23-55℃(73-130℉) CLTE, Parallel 23-55℃(73-130℉) Vicat Softening Temperature 50N |
ISO 11359-1/-2 ISO 11359-1/-2 ISO 306 |
E-4/C(E-4/F) E-4/C(E-4/F) ℃(℉) |
1(0.56) 0.2(0.11) 255(491) |
|
Electrical Surface Resistivity Relative Permittivity 1E6 Hz Volume Resistivity Dissipation Factor 1E6 Hz CTI CTI 3.0mm |
IEC 60093 IEC 60250 IEC 60093 IEC 60250 IEC 60112 UL 746A |
ohm ohm m E-4 V V |
>1E15 4.1 1E15 140 400 250 |
1E13 4.7 1E9 620 |
Flammability Flammability Classification 0.71mm Flammability Classification 0.71mm High Amperage Arc Ignition Resistance 0.71mm 1.5mm 3.0mm Hot Wire Ignition 0.71mm 1.5mm 3.0mm |
IEC 60695-11-10 UL94 UL 746A UL 746A |
arcs s |
HB HB 120 120 120 7 7 120 |
|
Property |
Test Method |
Units |
Value |
|
DAM |
50%RH |
|||
Temperature Index RTI, Electrical 0.71mm RTI, Impact 0.71mm RTI, Strength 0.71mm |
UL 746B UL 746B UL 746B |
℃ ℃ ℃ |
140 125 140 |
|
Other Density Ball Indention Hardness H 961/30 Hardness, Rockwell Scale M Scale R Water Absorption Equilibrium 50%RH Saturation, immersed Molding Shrinkage Normal, 2.0mm Parallel, 2.0mm |
ISO 1183 ISO 2039-1 ISO 2039/2 ISO 62, Similar to ISO 294-4 |
3 3 kg/m(g/cm ) MPa(kpsi) % % |
1410(1.41) 285(41) 105 125 1.7 5.5 1.1 0.3 |
203(29) 89 117 |
Processing Melt Temperature Range Melt Temperature Optimum Mold Temperature Range Mold Temperature Optimum Drying Time, Dehumidified Dryer Drying Temperature Processing Moisture Content |
℃(℉) ℃(℉) ℃(℉) ℃(℉) h ℃(℉) % |
285-305(545-580) 295(565) 70-120(160-250) 100(210) 2-4 80(175) <0.20 |
||
请联系无锡市达塑凯新材料有限公司的材料安全数据表，一般指南和/或有关通风，处理，吹扫，干燥等的其他信息ISO机械性能测量为4.0mm，ISO电气性能测量为2.0mm，所有ASTM性能测量为3.2mm。
除非另有说明，测试温度为23℃。
上述数据属于初步数据，随着后续批次的更多数据的发展而有所变化。