《电脑端可查看产品物性》
Zytel® 70G33L NC010 is a 33% glass fiber reinforced polyamide 66 resin for injection molding.
zytel®70G33L NC010是一个33%玻璃纤维增强聚酰胺66树脂注塑。
Property |
Test Method |
Units |
Value |
|
DAM |
50%RH |
|||
Identification Resin Identification Part Marking Code |
ISO 1043 ISO 11469 |
PA66-GF33 >PA66-GF33< |
||
Mechanical Stress at Break Strain at Break Tensile Modulus Poisson's Ratio Flexural Modulus Flexural Strength Notched Charpy Impact Strength -40℃(-40℉) -30℃(-22℉) 23℃(73℉) Unnotched Charpy Impact Strength -30℃(-22℉) 23℃(73℉) |
ISO 527 ISO 527 ISO 527 ISO 178 ISO 178 ISO 179/1eA ISO 179/1eU |
MPa(kpsi) % MPa(kpsi) MPa(kpsi) MPa(kpsi) 2 kJ/m 2 kJ/m |
200(29.0) 3.5 10500(1520) 0.39 9300(1350) 290(42) 10 10 13 70 85 |
140(20.3) 5 8000(1160) 6205(900) 200(29) 10 10 17 75 100 |
Property |
Test Method |
Units |
Value |
|
DAM |
50%RH |
|||
Thermal Deflection Temperature 0.45MPa 1.80MPa Melting Temperature 10℃/min CLTE, Normal -40-23℃(-40-73℉) 23-55℃(73-130℉) 55-160℃(130-320℉) CLTE, Parallel -40-23℃(-40-73℉) 23-55℃(73-130℉) 55-160℃(130-320℉) |
ISO 75f ISO 11357-1/-3 ISO 11359-1/-2 ISO 11359-1/-2 |
℃(℉) ℃(℉) E-4/C(E-4/F) E-4/C(E-4/F) |
261(502) 252(486) 262(504) 0.65(0.36) 0.83(0.46) 1.37(0.76) 0.24(0.13) 0.18(0.10) 0.13(0.07) |
|
Electrical Relative Permittivity 1E2 Hz 1E6 Hz Volume Resistivity Dissipation Factor 1E2 Hz 1E6 Hz CTI 3.0mm |
IEC 60250 IEC 60093 IEC 60250 UL 746A |
ohm m E-4 V |
4.2 4.0 1E13 100 150 600 |
|
Property |
Test Method |
Units |
Value |
|
DAM |
50%RH |
|||
Flammability Flammability Classification 0.71mm Oxygen Index High Amperage Arc Ignition Resistance 0.75mm High Voltage Arc Tracking Rate Hot Wire Ignition 0.71mm 1.5mm 3.0mm |
UL94 ISO 4589-1/-2 UL 746A UL 746A UL 746A |
% arcs mm/min(in/min) s |
HB 24 >200 32.2(1.27) 8 6 9 |
|
Temperature Index RTI, Electrical 0.71mm RTI, Impact 0.71mm RTI, Strength 0.71mm |
UL 746B UL 746B UL 746B |
℃ ℃ ℃ |
130 120 130 |
|
Other Density Water Absorption Equilibrium 50%RH Immersion 24h, 2.0mm Saturation, immersed Molding Shrinkage Normal, 2.0mm Parallel, 2.0mm |
ISO 1183 ISO 62, Similar to ISO 294-4 |
3 3 kg/m(g/cm ) % % |
1390(1.39) 1.8 1.2 5.7 1.1 0.3 |
|
Property |
Test Method |
Units |
Value |
|
DAM |
50%RH |
|||
Other Mold Shrinkage Flow, 1.6mm(0.063in) Flow, 3.2mm(0.126in) Flow, 6.4mm(0.25in) Transverse, 1.6mm(0.063in) Transverse, 3.2mm(0.126in) Transverse, 6.4mm(0.25in) |
% |
0.2 0.3 0.5 1.0 1.0 1.1 |
||
Processing Melt Temperature Range Melt Temperature Optimum Mold Temperature Range Mold Temperature Optimum Drying Time, Dehumidified Dryer Drying Temperature Processing Moisture Content |
℃(℉) ℃(℉) ℃(℉) ℃(℉) h ℃(℉) % |
285-305(545-580) 295(565) 70-120(160-250) 100(210) 2-4 80(175) <0.20 |
||
请联系无锡市达塑凯新材料有限公司的材料安全数据表，一般指南和/或有关通风，处理，吹扫，干燥等的其他信息ISO机械性能测量为4.0mm，ISO电气性能测量为2.0mm，所有ASTM性能测量为3.2mm。
除非另有说明，测试温度为23℃。