LEXAN™ EXL9134 resin
聚碳酸酯
产品说明：
LEXAN EXL9134 polycarbonate (PC) siloxane copolymer resin is a UV stabilized high flow opaque injection molding (IM) grade. This resin offers UL94 V0 @ 1.5mm flame retardancy based on non-bromine, non-chlorine FR systems, extreme low temperature ductility (-40 deg C) characteristics and excellent processability with opportunities for shorter IM cycle times compared to standard PC. LEXAN EXL9134 resin is a product available in a wide range of opaque colors and may be an excellent candidate for a wide range of applications.
LEXAN™ EXL9134 resin 物性表
| 基本信息 |
|
| 黄卡编号 |
|
| 添加剂 |
|
| 特性 |
Chlorine Free 共聚物 可加工性，良好 快的成型周期 流动性高 无溴 延展性 阻燃性 |
| RoHS 合规性 |
|
| 外观 |
|
| 加工方法 |
|
| 物理性能 |
额定值 |
单位制 |
测试方法 |
| 比重 |
1.19 |
g/cm3 |
ASTM D792, ISO 1183 |
| 熔流率（熔体流动速率） (300°C/1.2 kg) |
16 |
g/10 min |
ASTM D1238 |
| 溶化体积流率（MVR） (300°C/1.2 kg) |
15.1 |
cm3/10min |
ISO 1133 |
| 收缩率 - 流动 (3.20 mm) |
0.40 到 0.80 |
% |
内部方法 |
| 吸水率 |
|
|
ISO 62 |
| 饱和, 23°C |
0.40 |
% |
ISO 62 |
| 平衡, 23°C, 50% RH |
0.15 |
% |
ISO 62 |
| 室外适用性 |
f1 |
|
UL 746C |
| 机械性能 |
额定值 |
单位制 |
测试方法 |
| 拉伸模量 |
|
|
|
| -- 1 |
2100 |
MPa |
ASTM D638 |
| -- |
2000 |
MPa |
ISO 527-2/1 |
| 抗张强度 |
|
|
|
| 屈服 2 |
58.0 |
MPa |
ASTM D638 |
| 屈服 |
56.0 |
MPa |
ISO 527-2/50 |
| 断裂 3 |
59.0 |
MPa |
ASTM D638 |
| 断裂 |
57.0 |
MPa |
ISO 527-2/50 |
| 伸长率 |
|
|
|
| 屈服 4 |
6.0 |
% |
ASTM D638 |
| 屈服 |
6.0 |
% |
ISO 527-2/50 |
| 断裂 5 |
120 |
% |
ASTM D638 |
| 断裂 |
110 |
% |
ISO 527-2/50 |
| 弯曲模量 |
|
|
|
| 50.0 mm 跨距 6 |
2400 |
MPa |
ASTM D790 |
| -- 7 |
2100 |
MPa |
ISO 178 |
| 弯曲应力 |
|
|
|
| -- |
87.0 |
MPa |
ISO 178 |
| 屈服, 50.0 mm 跨距 8 |
92.0 |
MPa |
ASTM D790 |
| 冲击性能 |
额定值 |
单位制 |
测试方法 |
| 简支梁缺口冲击强度 9 |
|
|
ISO 179/1eA |
| -30°C |
35 |
kJ/m2 |
ISO 179/1eA |
| 23°C |
70 |
kJ/m2 |
ISO 179/1eA |
| 简支梁无缺口冲击强度 10 |
|
|
ISO 179/1eU |
| -30°C |
无断裂 |
|
ISO 179/1eU |
| 23°C |
无断裂 |
|
ISO 179/1eU |
| 悬壁梁缺口冲击强度 |
|
|
|
| -30°C |
660 |
J/m |
ASTM D256 |
| 23°C |
790 |
J/m |
ASTM D256 |
| -30°C 11 |
30 |
kJ/m2 |
ISO 180/1A |
| 23°C 12 |
65 |
kJ/m2 |
ISO 180/1A |
| 无缺口伊佐德冲击强度 13 |
|
|
ISO 180/1U |
| -30°C |
无断裂 |
|
ISO 180/1U |
| 23°C |
无断裂 |
|
ISO 180/1U |
| 装有测量仪表的落镖冲击 (23°C, Total Energy) |
67.0 |
J |
ASTM D3763 |
| 热性能 |
额定值 |
单位制 |
测试方法 |
| 载荷下热变形温度 |
|
|
|
| 1.8 MPa, 未退火, 3.20 mm |
123 |
°C |
ASTM D648 |
| 1.8 MPa, 未退火, 64.0 mm 跨距 14 |
118 |
°C |
ISO 75-2/Af |
| 维卡软化温度 |
|
|
|
| -- |
140 |
°C |
ASTM D1525 15 |
| -- |
139 |
°C |
ISO 306/B50 |
| -- |
141 |
°C |
ISO 306/B120 |
| Ball Pressure Test (125°C) |
Pass |
|
IEC 60695-10-2 |
| 线形热膨胀系数 |
|
|
ASTM E831, ISO 11359-2 |
| 流动 : -40 到 40°C |
6.1E-5 |
cm/cm/°C |
ASTM E831, ISO 11359-2 |
| 横向 : -40 到 40°C |
6.2E-5 |
cm/cm/°C |
ASTM E831, ISO 11359-2 |
| RTI Elec |
125 |
°C |
UL 746 |
| RTI Imp |
115 |
°C |
UL 746 |
| RTI |
120 |
°C |
UL 746 |
| 可燃性 |
额定值 |
单位制 |
测试方法 |
| UL 阻燃等级 |
|
|
UL 94 |
| 1.50 mm |
V-0 |
|
UL 94 |
| 3.00 mm |
5VA |
|
UL 94 |
| 灼热丝易燃指数 (1.50 mm) |
960 |
°C |
IEC 60695-2-12 |
| 热灯丝点火温度 |
|
|
IEC 60695-2-13 |
| 1.50 mm |
825 |
°C |
IEC 60695-2-13 |
| 3.00 mm |
825 |
°C |
IEC 60695-2-13 |
| 注射 |
额定值 |
单位制 |
|
| 干燥温度 |
120 |
°C |
|
| 干燥时间 |
3.0 到 4.0 |
hr |
|
| 干燥时间，最大 |
48 |
hr |
|
| 建议的最大水分含量 |
0.020 |
% |
|
| 建议注射量 |
40 到 60 |
% |
|
| 料筒后部温度 |
270 到 295 |
°C |
|
| 料筒中部温度 |
280 到 305 |
°C |
|
| 料筒前部温度 |
295 到 315 |
°C |
|
| 射嘴温度 |
290 到 310 |
°C |
|
| 加工（熔体）温度 |
295 到 315 |
°C |
|
| 模具温度 |
70.0 到 95.0 |
°C |
|
| 背压 |
0.300 到 0.700 |
MPa |
|
| 螺杆转速 |
40 到 70 |
rpm |
|
| 排气孔深度 |
0.025 到 0.076 |
mm |
|
| 备注 |
| 1 . |
5.0 mm/min |
| 2 . |
类型 1, 50 mm/min |
| 3 . |
类型 1, 50 mm/min |
| 4 . |
类型 1, 50 mm/min |
| 5 . |
类型 1, 50 mm/min |
| 6 . |
1.3 mm/min |
| 7 . |
2.0 mm/min |
| 8 . |
1.3 mm/min |
| 9 . |
80*10*3 sp=62mm |
| 10 . |
80*10*3 sp=62mm |
| 11 . |
80*10*3 |
| 12 . |
80*10*3 |
| 13 . |
80*10*3 |
| 14 . |
80*10*4 mm |
| 15 . |
标准 B (120°C/h), 载荷2 (50N) |