PBT LUBRICOMP WFL36

Physical Properties	Metric	English	Comments
Density	1.68 g/cc	0.0607 lb/in3	ASTM D792
	1.68 g/cc	0.0607 lb/in3	ISO 1183
Moisture Absorption	0.0400 %	0.0400 %	23°C / 50% RH; ISO 62
	0.0400 %	0.0400 %	50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow	0.0010 - 0.0030 cm/cm	0.0010 - 0.0030 in/in	24 hrs; ISO 294
	0.0010 - 0.0030 cm/cm	0.0010 - 0.0030 in/in	24 hrs; ASTM D955
Linear Mold Shrinkage, Transverse	0.0050 - 0.010 cm/cm	0.0050 - 0.010 in/in	24 hrs; ASTM D955
	0.0050 - 0.010 cm/cm	0.0050 - 0.010 in/in	24 hrs; ISO 294
Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	117 MPa	17000 psi	ASTM D638
	118 MPa	17100 psi	ISO 527
Elongation at Break	2.2 %	2.2 %	ISO 527
	2.3 %	2.3 %	ASTM D638
Flexural Strength	187 MPa	27100 psi	ISO 178
	193 MPa	28000 psi	ASTM D790
Flexural Modulus	10.01 GPa	1452 ksi	ISO 178
	10.16 GPa	1474 ksi	ISO 178/1A
Izod Impact, Notched	0.960 J/cm	1.80 ft-lb/in	ASTM D256

PBT LUBRICOMP WFL36

特性

PBT是最坚韧的工程热塑材料之一，它是半结晶材料，有非常好的化学稳定性、机械强度、电绝缘特性和热稳定性。这些材料在很广的环境条件下都有很好的稳定性。PBT吸湿特性很弱。非增强型PBT的张力强度为50MPa，玻璃添加剂型的PBT张力强度为170MPa。玻璃添加剂过多将导致材料变脆。PBT的结晶很迅速，这将导致因冷却不均匀而造成弯曲变形。对于有玻璃添加剂类型的材料，流程方向的收缩率可以减小，但与流程垂直方向的收缩率基本上和普通材料没有区别。一般材料收缩率在1.5%~2.8%之间。含30%玻璃添加剂的材料收缩0.3%~1.6%之间。熔点（225℃）和高温变形温度都比PET材料要低。维卡软化温度大约为170℃。玻璃化转换温度（glass trasitio temperature）在22℃到43℃之间。由于PBT的结晶速度很高，因此它的粘性很低，塑件加工的周期时间一般也较低。

三、PBT塑料的粘接：

　　根据不同需要，可以选择以下粘合剂：

　　1. TG-3200：单组分常温固化软弹性防震粘合剂，耐高低温，但粘接速度慢，胶水通常要1天或几天时间才能固化完毕。

　　2. TS-8602瞬间粘接剂，可以数秒钟或数十秒钟快速粘合PBT，但胶层硬脆，不耐水。

　　3. TE-9270类，双组分胶，胶层柔软，适合PBT大面积粘接或复合。但耐高温性能较差。

　　4.TE-9249类胶：双组分胶，耐高温。

应用范围

家用器具（食品加工刀片、真空吸尘器元件、电风扇、头发干燥机壳体、咖啡器皿等），电器元件（开关、电机壳、保险丝盒、计算机键盘按键等），汽车工业（散热器格窗、车身嵌板、车轮盖、门窗部件等）。