PBT LUBRICOMP WI001

Physical Properties	Metric	English	Comments
Specific Gravity	1.30 g/cc	1.30 g/cc	ASTM D792
Density	1.30 g/cc	0.0470 lb/in3	ASTM D792
Moisture Absorption	0.0600 %	0.0600 %	50% RH, 24 hrs; ASTM D570
	0.0900 %	0.0900 %	(23°C / 50% RH; ISO 62
Maximum Moisture Content	0.050	0.050
Linear Mold Shrinkage, Flow	0.020 - 0.040 cm/cm @Time 86400 sec	0.020 - 0.040 in/in @Time 24.0 hour	ASTM D955
Linear Mold Shrinkage, Transverse	0.020 - 0.040 cm/cm @Time 86400 sec	0.020 - 0.040 in/in @Time 24.0 hour	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	45.0 MPa	6530 psi	5 mm/min; ISO 527
	46.0 MPa	6670 psi	Type I, 5 mm/min; ASTM D638
Tensile Strength, Yield	50.0 MPa	7250 psi	Type I, 5 mm/min; ASTM D638
	53.0 MPa	7690 psi	5 mm/min; ISO 527
Elongation at Break	32 %	32 %	5 mm/min; ISO 527
	51 %	51 %	Type I, 5 mm/min; ASTM D638
Elongation at Yield	2.8 %	2.8 %	Type I, 5 mm/min; ASTM D638
	3.0 %	3.0 %	5 mm/min; ISO 527
Tensile Modulus	2.54 GPa	368 ksi	1mm/min; ISO 527
	2.72 GPa	395 ksi	5 mm/min; ASTM D638
Flexural Strength	81.0 MPa	11700 psi	ISO 178
Flexural Yield Strength	88.0 MPa	12800 psi	1.3 mm/min, 50 mm span; ASTM D790

PBT LUBRICOMP WI001 可提供COA、COC,ROHS.MSDS.UL黄卡等等资料，价格最优，质量保证！

PBT中文名称聚对苯二甲酸丁酯，简称饱和聚酯，系高结晶性热可塑性塑料。

优点：1、机械性质安定抗张强度与抗张模量和尼龙相似；2、摩擦系数小有自润性；

3、吸水率低；4、电气性质优良；5、尺寸安定性良好；6、耐药品性、耐油性极佳。

用途：1、电子电器：无熔线断电器、电磁开关、驰返变压器、家电把手、连接器、外壳等；

2、汽车：车门把手、保险杆、分电盘盖、挡泥板、导线护壳、轮圈盖等；

3、工业零件：OA风扇、键盘、钓具卷线器、零件、灯罩等。

特点：PBT为乳白色半透明到不透明、结晶型热塑性聚酯。具有高耐热性、韧性、耐疲劳性，自润滑、低摩擦系数，耐候性、吸水率低，仅为0.1%，在潮湿环境中仍保持各种物性（包括电性能），电绝缘性，但介电损耗大。耐热水、碱类、酸类、油类、但易受卤化烃侵蚀，耐水解性差，低温下可迅速结晶，成型性良好。PBT 结晶速度快，最适宜加工方法为注塑，其他方法还有挤出、吹塑、涂覆和各种二次加工成型，成型前需预干燥，水分含量要降至0.02%。PBT（增强、改性PBT）主要用于汽车、电子电器、工业机械和聚合物合金、共混工业。如作为汽车中的分配器、车体部件、点火器线圈骨架、绝缘盖、排气系统零部件、摩托车点火器、电子电器工业中如电视机的偏转线圈，显像管和电位器支架，伴音输出变压器骨架，适配器骨架，开关接插件、电风扇、电冰箱、洗衣机电机端盖、轴套.