PBT LUBRICOMP WX12001J

Physical Properties	Metric	English	Comments
Density	1.34 g/cc	0.0484 lb/in3	ISO 1183
Moisture Absorption at Equilibrium	0.060 %	0.060 %	50% RH, 24 hrs; ISO 62-4
Melt Flow	25 g/10 min @Load 2.16 kg, Temperature 250 °C	25 g/10 min @Load 4.76 lb, Temperature 482 °F	MVR, cm^3/10 min; ISO 1133
Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	54.0 MPa	7830 psi	50 mm/min; ISO 527
Tensile Strength, Yield	56.0 MPa	8120 psi	50 mm/min; ISO 527
Elongation at Break	13 %	13 %	50 mm/min; ISO 527
Elongation at Yield	10 %	10 %	50 mm/min; ISO 527
Flexural Strength	80.0 MPa	11600 psi	ISO 178
Flexural Modulus	2.30 GPa	334 ksi	2 mm/min; ISO 178
Izod Impact, Notched (ISO)	3.00 kJ/m2	1.43 ft-lb/in2	80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO)	47.0 kJ/m2	22.4 ft-lb/in2	80*10*4; ISO 180/1U
Charpy Impact, Notched	0.400 J/cm2	1.90 ft-lb/in2	Edgew 80*10*4 sp=62mm; ISO 179/1eA
Coefficient of Friction, Dynamic	0.31	0.31	ASTM D3702 Modified: Instr.
Coefficient of Friction, Static	0.48	0.48	ASTM D3702 Modified: Instr.
K (wear) Factor	224 x 10-8 mm3/N-M	111 x 10-10 in3-min/ft-lb-hr	Washer; ASTM D3702 Modified: Instr.
Tangent Modulus	2500 MPa	363000 psi	1 mm/min; ISO 527

PBT LUBRICOMP WX12001J

PBT中文名称聚对苯二甲酸丁酯，简称饱和聚酯，系高结晶性热可塑性塑料。

优点：1、机械性质安定抗张强度与抗张模量和尼龙相似；2、摩擦系数小有自润性；

3、吸水率低；4、电气性质优良；5、尺寸安定性良好；6、耐药品性、耐油性极佳。

用途：1、电子电器：无熔线断电器、电磁开关、驰返变压器、家电把手、连接器、外壳等；

2、汽车：车门把手、保险杆、分电盘盖、挡泥板、导线护壳、轮圈盖等；

3、工业零件：OA风扇、键盘、钓具卷线器、零件、灯罩等。

特点：PBT为乳白色半透明到不透明、结晶型热塑性聚酯。具有高耐热性、韧性、耐疲劳性，自润滑、低摩擦系数，耐候性、吸水率低，仅为0.1%，在潮湿环境中仍保持各种物性（包括电性能），电绝缘性，但介电损耗大。耐热水、碱类、酸类、油类、但易受卤化烃侵蚀，耐水解性差，低温下可迅速结晶，成型性良好。PBT 结晶速度快，最适宜加工方法为注塑，其他方法还有挤出、吹塑、涂覆和各种二次加工成型，成型前需预干燥，水分含量要降至0.02%。PBT（增强、改性PBT）主要用于汽车、电子电器、工业机械和聚合物合金、共混工业。如作为汽车中的分配器、车体部件、点火器线圈骨架、绝缘盖、排气系统零部件、摩托车点火器、电子电器工业中如电视机的偏转线圈，显像管和电位器支架，伴音输出变压器骨架，适配器骨架，开关接插件、电风扇、电冰箱、洗衣机电机端盖、轴套.

PBT LUBRICOMP WX12001J 可提供COA、COC,ROHS.MSDS.UL黄卡等等资料，价格最优，质量保证！