PA66 （尼龙66）Zytel 80G14AHS NC010

Physical Properties	Metric	English	Comments
Density	1.19 g/cc	0.0430 lb/in3	DAM; ISO 1183
Moisture Absorption	1.90 % @Thickness 2.00 mm	1.90 % @Thickness 0.0787 in	DAM; Sim. to ISO 62
Linear Mold Shrinkage, Flow	0.0040 cm/cm	0.0040 in/in	DAM; ISO 294-4, 2577
Linear Mold Shrinkage, Transverse	0.0080 cm/cm	0.0080 in/in	DAM; ISO 294-4, 2577
Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	72.0 MPa	10400 psi	50% RH; ISO 527-1/-2
	110 MPa	16000 psi	DAM; ISO 527-1/-2
Elongation at Break	3.8 %	3.8 %	DAM; ISO 527-1/-2
	6.0 %	6.0 %	50% RH; ISO 527-1/-2
Tensile Modulus	3.30 GPa	479 ksi	50% RH; ISO 527-1/-2
	5.00 GPa	725 ksi	DAM; ISO 527-1/-2
Flexural Modulus	3.12 GPa	453 ksi	50% RH; ISO 178
	4.40 GPa	638 ksi	DAM; ISO 178
Poissons Ratio	0.35	0.35	DAM; ISO 527-1/-2
	0.37	0.37	50%RH; ISO 527-1/-2

PA66（尼龙66） Zytel 80G14AHS NC010

尼龙中的主要品种是尼龙6和尼龙66，占绝对主导地位，尼龙6为聚己内酰胺，而尼龙66为聚己二酸己二胺，尼龙66比尼龙6要硬l2%；其次是尼龙11，尼龙12，尼龙610，尼龙612，另外还有尼龙1010、尼龙46、尼龙7、尼龙9、尼龙13，新品种有尼龙6I、尼龙9T和特殊尼龙MXD6（阻隔性树脂）等，尼龙的改性品种数量繁多，如增强尼龙、单体浇铸尼龙（MC尼龙）、反应注射成型(RIM)尼龙、芳香族尼龙、透明尼龙、高抗冲（超韧）尼龙、电镀尼龙、导电尼龙、阻燃尼龙，尼龙与其他聚合物共混物和合金等，满足不同特殊要求，广泛用作金属，木材等传统材料代用品。

尼龙66特性

尼龙66作为大用量的工程塑料，广泛用于机械、汽车、电器、纺织器材、化工设备、航空、冶金等领域。

成为各行业中不可缺少的结构材料，其主要特点如下：

1．优良的力学性能。尼龙的机械强度高，韧性好。

2．自润性、耐摩擦性好。尼龙具有很好的自润划性，摩擦系数小，从而，作为传动部件其使用寿命长。

3.优良的耐热性。如尼龙46等高结晶性尼龙的热变形温度很高，可在150℃下长期期使用。PA66经过

玻璃纤维增强以后，其热变形温度达到250℃以上。

4.优异的电绝缘性能。尼龙的体积电阻很高，耐击穿电压高，是优良的电气、电器绝缘材料。

5.优良的耐气候性。

6.吸水性。尼龙吸水性大，饱和吸水可达到3%以上。在一定程度影响制件的尺寸稳定性。

尼龙66的应用

高温电气插座零件、电气零件、齿轮、轴承、滚子、弹簧支架、滑轮、螺栓、叶轮、风扇叶片、螺旋桨、高压封口垫片、阀座、输油管、储油容器、绳索、扎带、传动皮带、砂轮粘合剂、电池箱、绝缘电气零件、线芯、抽丝等