POM THERMOCOMP KFB11

Physical Properties	Metric	English	Comments
Density	1.48 g/cc	0.0535 lb/in3	ASTM D792
	1.48 g/cc	0.0535 lb/in3	ISO 1183
Moisture Absorption	0.200 %	0.200 %	50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow	0.019 cm/cm	0.019 in/in	24 hrs; ISO 294
	0.010 - 0.030 cm/cm	0.010 - 0.030 in/in	24 hrs; ASTM D955
Linear Mold Shrinkage, Transverse	0.017 cm/cm	0.017 in/in	24 hrs; ISO 294
	0.010 - 0.030 cm/cm	0.010 - 0.030 in/in	24 hrs; ASTM D955
Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	60.0 MPa	8700 psi	ISO 527
	62.0 MPa	8990 psi	ASTM D638
Tensile Strength, Yield	64.0 MPa	9280 psi	ASTM D638
	65.0 MPa	9430 psi	ISO 527
Elongation at Break	5.7 %	5.7 %	ASTM D638
	7.0 %	7.0 %	ISO 527
Elongation at Yield	3.9 %	3.9 %	ISO 527
	4.0 %	4.0 %	ASTM D638
Flexural Strength	91.0 MPa	13200 psi	ISO 178
Flexural Modulus	3.00 GPa	435 ksi	ISO 178
	3.44 GPa	499 ksi	ISO 178/1A
Izod Impact, Notched	0.530 J/cm	0.993 ft-lb/in	ASTM D256
Izod Impact, Unnotched	5.28 J/cm	9.89 ft-lb/in	ASTM D4812
Izod Impact, Notched (ISO)	5.00 kJ/m2	2.38 ft-lb/in2	80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO)	35.0 kJ/m2	16.7 ft-lb/in2	80*10*4; ISO 180/1U
Impact Test	1.00 J	0.738 ft-lb	Multiaxial Impact; ISO 6603

POM THERMOCOMP KFB11

特性

POM是一种坚韧有弹性的材料，即使在低温下仍有很好的抗蠕变特性、几何稳定性和抗冲击特性。POM既有均聚物材料也有共聚物材料。均聚物材料具有很好的延展强度、抗疲劳强度，但不易于加工。共聚物材料有很好的热稳定性、化学稳定性并且易于加工。无论均聚物材料还是共聚物材料，都是结晶性材料并且不易吸收水分。POM的高结晶程度导致它有相当高的收缩率，可高达到2%~3.5%。对于各种不同的增强型材料有不同的收缩率。

用途

聚甲醛（POM）是一种性能优良的工程塑料，在国外有“夺钢”、

聚甲醛制品2

超钢”之称。POM具有类似金属的硬度、强度和钢性，在很宽的温度和湿度范围内都具有很好的自润滑性、良好的耐疲劳性，并富于弹性，此外它还有较好的耐化学品性。POM以低于其他许多工程塑料的成本，正在替代一些传统上被金属所占领的市场，如替代锌、黄铜、铝和钢制作许多部件，自问世以来，POM已经广泛应用于电子电气、机械、仪表、日用轻工、汽车、建材、农业等领域。在很多新领域的应用，如医疗技术、运动器械等方面，POM也表现出较好的增长态势。