PA6 Zytel ST7301 BK356
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.06 g/cc | 0.0383 lb/in3 | DAM; ISO 1183 |
| Moisture Absorption | 2.70 % @Thickness 2.00 mm |
2.70 % @Thickness 0.0787 in |
DAM; Sim. to ISO 62 |
| Linear Mold Shrinkage, Flow | 0.013 cm/cm | 0.013 in/in | DAM; ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.013 cm/cm | 0.013 in/in | DAM; ISO 294-4, 2577 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 30.0 MPa | 4350 psi | 50% RH; ISO 527-1/-2 |
| 48.0 MPa | 6960 psi | DAM; ISO 527-1/-2 | |
| Elongation at Break | 45 % | 45 % | DAM; ISO 527-1/-2 |
| >= 50 % | >= 50 % | 50% RH; ISO 527-1/-2 | |
| Elongation at Yield | 4.0 % | 4.0 % | DAM; ISO 527-1/-2 |
| 33 % | 33 % | 50% RH; ISO 527-1/-2 | |
| Tensile Modulus | 0.550 GPa | 79.8 ksi | 50% RH; ISO 527-1/-2 |
| 1.80 GPa | 261 ksi | DAM; ISO 527-1/-2 | |
| Flexural Modulus | 0.550 GPa | 79.8 ksi | 50% RH; ISO 178 |
| 1.80 GPa | 261 ksi | DAM; ISO 178 | |
PA6 Zytel ST7301 BK356
PA6特性：
聚酰胺-6的化学物理特性和尼龙66很相似，然而，它的熔点较低，而且工艺温度范围很宽。它的抗冲击性和抗溶解性比尼龙66塑料要好,但吸湿性也更强。因为塑件的许多品质特性都要受到吸湿性的影响，因此使用尼龙6设计产品时要充分考虑到这一点。为了提高尼龙6的机械特性，经常加入各种各样的改性剂。玻璃就是最常见的添加剂，有时为了提高抗冲击性还加入合成橡胶，如EPDM和SBR等。对于没有添加剂的产品，尼龙6塑胶原料的收缩率在1%到1.5%之间。加入玻璃纤维添加剂可以使收缩率降低到0.3%（但和流程相垂直的方向还要稍高一些）。成型组装的收缩率主要受材料结晶度和吸湿性影响。实际的收缩率还和塑件设计、壁厚及其它工艺参数成函数关系。尼龙6注塑干燥处理由于尼龙6很容易吸收水分.
PA6用途:
该类产品用途广，是以塑代钢、铁、铜等金属的好材料，是重要的工程塑料；铸型尼龙广泛代替机械设备的耐磨部件，代替铜和合金作设备的耐磨损件。适用于制作耐磨零件，传动结构件，家用电器零件，汽车制造零件，丝杆防止机械零件，化工机械零件，化工设备。如涡轮、齿轮、轴承、叶轮、曲柄、仪表板，驱动轴，阀门、叶片、丝杆、高压垫圈、螺丝、螺母、密封圈，梭子、套简，轴套连接器等。