Vydyne® R533H
聚酰胺66
33% 玻璃纤维增强材料
Ascend Performance Materials Operations LLC
产品说明：
Vydyne R533H is 33% glass-fiber reinforced, heat-stabilized PA66 resin. Available in natural, it is specifically designed to maximize the retention of physical properties when exposed to anti-freeze solutions at elevated temperatures. This product is lubricated for improved machine feed and flow.
Glass-reinforced Vydyne resins provide higher heat distortion temperature, resistance to creep and better dimensional stability when compared with unreinforced PA66. These products have good chemical resistance to a broad range of chemicals including gasoline, hydraulic fluids and most solvents.
Vydyne R533H resin is heat-stabilized to minimize oxidative degradation of the polymer when exposed to elevated temperatures in service. This product provides improved retention of physical properties under exposure to long-term heat. Also, Vydyne R533H resin has excellent knit-line strength and fatigue resistance, which is essential for cycle testing with anti-freeze solutions.
Typical Applications/End Uses:
Vydyne R533H resin has been used for many under-the-hood automotive applications, motor housings for power tools and garden appliances. This resin has also been used in miscellaneous brackets, gears and clips that require high rigidity and strength.
Vydyne® R533H 物性表
基本信息 |
|
填料/增强材料 |
· 玻璃纤维增强材料, 33% 填料按重量 |
添加剂 |
· 热稳定剂 · 润滑剂 |
特性 |
· 刚性，高 · 高强度 · 流动性高 · 热稳定性 · 润滑 · 脱模性能良好 |
用途 |
· 齿轮 · 动力/其它工具 · 汽车的发动机罩下的零件 · 外壳 |
机构评级 |
· ASTM D 4066 PA0121G35 · ASTM D 6779 PA0121G35 |
UL文件号 |
· E70062 |
外观 |
· 自然色 |
形式 |
· 粒子 |
加工方法 |
· 注射成型 |
物理性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
密度 |
1.40 |
-- |
g/cm3 |
ISO 1183 |
收缩率 |
ISO 294-4 |
|||
垂直流动方向 : 23°C, 2.00 mm |
0.90 |
-- |
% |
ISO 294-4 |
流动方向 : 23°C, 2.00 mm |
0.40 |
-- |
% |
ISO 294-4 |
吸水率 |
ISO 62 |
|||
23°C, 24 hr |
0.80 |
-- |
% |
ISO 62 |
平衡, 23°C, 50% RH |
1.7 |
-- |
% |
ISO 62 |
机械性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
拉伸模量 (23°C) |
10600 |
7900 |
MPa |
ISO 527-2 |
拉伸应力 (断裂, 23°C) |
205 |
145 |
MPa |
ISO 527-2 |
拉伸应变 (断裂, 23°C) |
3.0 |
5.0 |
% |
ISO 527-2 |
弯曲模量 (23°C) |
10200 |
6500 |
MPa |
ISO 178 |
弯曲应力 (23°C) |
290 |
200 |
MPa |
ISO 178 |
泊松比 |
0.40 |
-- |
ISO 527-2 |
冲击性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
简支梁缺口冲击强度 |
ISO 179/1eA |
|||
-30°C |
10 |
12 |
kJ/m2 |
ISO 179/1eA |
23°C |
11 |
14 |
kJ/m2 |
ISO 179/1eA |
简支梁无缺口冲击强度 |
ISO 179/1eU |
|||
-30°C |
70 |
85 |
kJ/m2 |
ISO 179/1eU |
23°C |
80 |
90 |
kJ/m2 |
ISO 179/1eU |
悬壁梁缺口冲击强度 |
ISO 180 |
|||
-30°C |
10 |
12 |
kJ/m2 |
ISO 180 |
23°C |
12 |
14 |
kJ/m2 |
ISO 180 |
热性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
热变形温度 |
||||
0.45 MPa, 未退火 |
260 |
-- |
°C |
ISO 75-2/B |
1.8 MPa, 未退火 |
250 |
-- |
°C |
ISO 75-2/A |
熔融温度 |
260 |
-- |
°C |
ISO 11357-3 |
线形热膨胀系数 |
ISO 11359-2 |
|||
流动 : 23 到 55°C, 2.00 mm |
2.1E-5 |
-- |
cm/cm/°C |
ISO 11359-2 |
横向 : 23 到 55°C, 2.00 mm |
1.1E-4 |
-- |
cm/cm/°C |
ISO 11359-2 |
RTI Elec |
UL 746 |
|||
0.750 mm |
140 |
-- |
°C |
UL 746 |
1.50 mm |
140 |
-- |
°C |
UL 746 |
3.00 mm |
140 |
-- |
°C |
UL 746 |
RTI Imp |
UL 746 |
|||
0.750 mm |
125 |
-- |
°C |
UL 746 |
1.50 mm |
125 |
-- |
°C |
UL 746 |
3.00 mm |
125 |
-- |
°C |
UL 746 |
RTI |
UL 746 |
|||
0.750 mm |
140 |
-- |
°C |
UL 746 |
1.50 mm |
140 |
-- |
°C |
UL 746 |
3.00 mm |
140 |
-- |
°C |
UL 746 |
电气性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
体积电阻率 (0.750 mm) |
1.0E+13 |
-- |
ohms·cm |
IEC 60093 |
介电强度 (1.00 mm) |
20 |
-- |
kV/mm |
IEC 60243 |
耐电弧性 (3.00 mm) |
PLC 6 |
-- |
ASTM D495 |
|
漏电起痕指数 (3.00 mm) |
250 到 399 |
-- |
V |
IEC 60112 |
高电弧燃烧指数(HAI) |
UL 746 |
|||
0.750 mm |
PLC 0 |
-- |
UL 746 |
|
1.50 mm |
PLC 0 |
-- |
UL 746 |
|
3.00 mm |
PLC 0 |
-- |
UL 746 |
|
高电压电弧起痕速率 (HVTR) |
PLC 1 |
-- |
UL 746 |
|
热丝引燃 (HWI) |
UL 746 |
|||
0.750 mm |
PLC 4 |
-- |
UL 746 |
|
1.50 mm |
PLC 3 |
-- |
UL 746 |
|
3.00 mm |
PLC 4 |
-- |
UL 746 |
可燃性 |
干燥 |
调节后的 |
单位制 |
测试方法 |
UL 阻燃等级 |
UL 94 |
|||
0.750 mm |
HB |
-- |
UL 94 |
|
1.50 mm |
HB |
-- |
UL 94 |
|
3.00 mm |
HB |
-- |
UL 94 |
|
灼热丝易燃指数 |
IEC 60695-2-12 |
|||
0.750 mm |
675 |
-- |
°C |
IEC 60695-2-12 |
1.50 mm |
675 |
-- |
°C |
IEC 60695-2-12 |
3.00 mm |
675 |
-- |
°C |
IEC 60695-2-12 |
热灯丝点火温度 |
IEC 60695-2-13 |
|||
0.750 mm |
700 |
-- |
°C |
IEC 60695-2-13 |
1.50 mm |
700 |
-- |
°C |
IEC 60695-2-13 |
3.00 mm |
700 |
-- |
°C |
IEC 60695-2-13 |
注射 |
干燥 |
单位制 |
|
干燥温度 |
80.0 |
°C |
|
干燥时间 |
4.0 |
hr |
|
建议的最大回制料比例 |
25 |
% |
|
料筒后部温度 |
280 到 310 |
°C |
|
料筒中部温度 |
280 到 310 |
°C |
|
料筒前部温度 |
280 到 310 |
°C |
|
射嘴温度 |
280 到 310 |
°C |
|
加工（熔体）温度 |
285 到 305 |
°C |
|
模具温度 |
65.0 到 95.0 |
°C |