东莞市恒磊塑胶有限公司
PP LATENE EP 7 TES/30
| Material Notes: | Polypropylene copolymer (PPc) based compound. Aesthetic talc. Very good surface appearance. Good elongation. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North America Information provided by Lati Industria Termoplastici S.p.A. |
| Vendors: | No vendors are listed for this material. Please click here if you are a supplier and would like information on how to add your listing to this material. |
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in3 | |
| Linear Mold Shrinkage, Flow | 0.0095 - 0.0125 cm/cm | 0.0095 - 0.0125 in/in | |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.013 cm/cm | 0.010 - 0.013 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 15.0 MPa | 2180 psi | |
| Elongation at Break | 35 % @Temperature 23.0 °C |
35 % @Temperature 73.4 °F |
|
| >= 100 % @Temperature 60.0 °C |
>= 100 % @Temperature 140 °F |
||
| >= 100 % @Temperature 90.0 °C |
>= 100 % @Temperature 194 °F |
||
| Elongation at Yield | 3.0 % @Temperature 23.0 °C |
3.0 % @Temperature 73.4 °F |
|
| 5.0 % @Temperature 60.0 °C |
5.0 % @Temperature 140 °F |
||
| 6.0 % @Temperature 90.0 °C |
6.0 % @Temperature 194 °F |
||
| Tensile Modulus | 0.500 GPa @Temperature 90.0 °C |
72.5 ksi @Temperature 194 °F |
|
| 1.10 GPa @Temperature 60.0 °C |
160 ksi @Temperature 140 °F |
||
| 2.60 GPa @Temperature 23.0 °C |
377 ksi @Temperature 73.4 °F |
||
| Charpy Impact Unnotched | 1.50 J/cm2 @Temperature -20.0 °C |
7.14 ft-lb/in2 @Temperature -4.00 °F |
|
| 3.00 J/cm2 @Temperature 23.0 °C |
14.3 ft-lb/in2 @Temperature 73.4 °F |
||
| Charpy Impact, Notched | 0.0300 J/cm2 @Temperature -20.0 °C |
0.143 ft-lb/in2 @Temperature -4.00 °F |
|
| 0.200 J/cm2 @Temperature 23.0 °C |
0.952 ft-lb/in2 @Temperature 73.4 °F |
||