PP LATENE AG3H2W G/30-V0E
Material Notes: | Polypropylene homopolymer (PPh) based compound. Chemical grafting Heat stabilized. Metal stabilized. Glass fibers. UL94 V-0 classified, with brominated flame retardants, PBB/PBDE free Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North America Information provided by Lati Industria Termoplastici S.p.A. |
Vendors: | No vendors are listed for this material. Please click here if you are a supplier and would like information on how to add your listing to this material. |
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 1.46 g/cc | 0.0527 lb/in3 | |
Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm | 0.0030 - 0.0050 in/in | |
Linear Mold Shrinkage, Transverse | 0.0075 - 0.0095 cm/cm | 0.0075 - 0.0095 in/in | |
Mechanical Properties | Metric | English | Comments |
Tensile Strength at Break | 30.0 MPa @Temperature 90.0 °C |
4350 psi @Temperature 194 °F |
|
45.0 MPa @Temperature 60.0 °C |
6530 psi @Temperature 140 °F |
||
75.0 MPa @Temperature 23.0 °C |
10900 psi @Temperature 73.4 °F |
||
Elongation at Break | 2.5 % @Temperature 23.0 °C |
2.5 % @Temperature 73.4 °F |
|
4.0 % @Temperature 60.0 °C |
4.0 % @Temperature 140 °F |
||
7.0 % @Temperature 90.0 °C |
7.0 % @Temperature 194 °F |
||
Elongation at Yield | 2.5 % @Temperature 60.0 °C |
2.5 % @Temperature 140 °F |
|
4.0 % @Temperature 90.0 °C |
4.0 % @Temperature 194 °F |
||
Tensile Modulus | 4.30 GPa @Temperature 90.0 °C |
624 ksi @Temperature 194 °F |
|
5.70 GPa @Temperature 60.0 °C |
827 ksi @Temperature 140 °F |
||
7.80 GPa @Temperature 23.0 °C |
1130 ksi @Temperature 73.4 °F |
||
Charpy Impact Unnotched | 2.00 J/cm2 @Temperature -20.0 °C |
9.52 ft-lb/in2 @Temperature -4.00 °F |
|
4.00 J/cm2 @Temperature 23.0 °C |
19.0 ft-lb/in2 @Temperature 73.4 °F |
||
Charpy Impact, Notched | 0.500 J/cm2 @Temperature -20.0 °C |
2.38 ft-lb/in2 @Temperature -4.00 °F |
|
1.00 J/cm2 @Temperature 23.0 °C |
4.76 ft-lb/in2 @Temperature 73.4 °F |