TPO DAPLEN EE158AI
Daplen™ EE158AI is a 13% mineral filled elastomer modified polypropylene compound intended for injection molding. This material has an excellent balance between impact strength and stiffness, gives a good surface quality and is easy to process. Applications: Daplen™ EE158AI has been developed especially for the car industry to be used in automotive interior parts including dashboards, pillar trims, door panels and pockets, trunk claddings and other automotive interior parts
Information provided by Borealis AG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.980 g/cc | 0.0354 lb/in3 | ISO 1183 |
| Linear Mold Shrinkage | 0.00090 cm/cm | 0.00090 in/in | Borealis Method; anisotropic shrinkage |
| 0.0090 cm/cm | 0.0090 in/in | Borealis Method; isotropic shrinkage | |
| Melt Flow | 11 g/10 min @Load 2.16 kg, Temperature 230 °C |
11 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 23.0 MPa | 3340 psi | 50mm/min; ISO 527-2 |
| Elongation at Yield | 6.0 % | 6.0 % | 50mm/min; ISO 527-2 |
| Tensile Modulus | 1.70 GPa | 247 ksi | 1mm/min; ISO 527-2 |
| Flexural Strength | 30.0 MPa | 4350 psi | ISO 178 |
| Flexural Modulus | 1.75 GPa | 254 ksi | 2mm/min; ISO 178 |
| Charpy Impact Unnotched | 6.00 J/cm2 @Temperature -20.0 °C |
28.6 ft-lb/in2 @Temperature -4.00 °F |
ISO 179/1eU |
| 17.0 J/cm2 @Temperature 23.0 °C |
80.9 ft-lb/in2 @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.500 J/cm2 @Temperature -20.0 °C |
2.38 ft-lb/in2 @Temperature -4.00 °F |
ISO 179/1eA |
| 2.50 J/cm2 @Temperature 23.0 °C |
11.9 ft-lb/in2 @Temperature 73.4 °F |
ISO 179/1eA | |
TPO DAPLEN EE158AI
TPO的两大分类按照合成的方式，将TPO分为聚合类及共混类两种。
(1).聚合类TPO
两种（或以上）聚合物单体，发生共聚合反应，生成的聚合物。聚合物一部分分子链段发生结晶，另一部分链段保持柔顺性，使得材料同时具有刚性和弹性的链段，具有热塑性弹性体的物理交联结构。如以上提到的POE就是典型的案例，另外EVA等也是。
(2).共混类TPO
这类TPO是橡胶与聚烯烃通过物理共混的方式，合成出的一种烯烃类弹性体。常见的共混品种为PP/POE,PP/EPDM,PP/NBR,PVC/NBR等。其中，PP/EPDM之共混，除一般意义的共混外，还有动态硫化共混方式，后者在弹性体行业又称为TPV,Thermoplastic Vulcanizate，意思是热塑性动态硫化橡胶。TPV是特殊的一类TPO,也是目前最成功和广泛应用的TPO,以至于有单独的名称TPV.
TPO材料主要特性
外观：本色、透明、(雾)黑颗粒；硬度：ShoreA50~64D
3.1.具有耐紫外线和臭氧，耐温性-60℃到135℃。
3.2.TPO材料手感细腻，优异的耐老化性，耐酸、碱、醇类溶剂化学品。
3.3.低密度-0.95，表面雾面(哑光)非常好，一般TPE/TPR材料达不到的效果。
3.4.环保型材料，高耐撕裂性能，低压缩变形性。
TPO主要应用领域
电缆、轻纺、建筑、家电领域；
汽车部件：玻璃封边、引擎盖密封、软管、车灯罩、防尘罩、防尘座、安全气囊等；
机械工具：手柄、握把、胶辊、接管接头、玻璃密封等。
TPO只是热塑性弹性体TPE的一种，除TPO外，热塑性弹性体TPE还包括TPU,TPES（TPR),TPV,TPAE,TPEE等等。