东莞市塑宇化工有限公司
PA6(聚已内酰胺#尼龙6)/1011FB/泰国宇部
用途： 其它
特性备注：特性：低粘度，高流动，脱模
重要参数： 密度:1.14 g/cm3 成型收缩率:1.4 % 断裂伸长率:200 % 弯曲强度:107.84 MPa 弯曲模量:2549.02 MPa 硬度:120 热变形温度:75 ℃
生产厂商：日本宇部亚洲化学公司
产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 机械性能 | 弯曲弹性率 | 23° | ASTM D-790 | 7500 | kgf/cm2 |
| 硬度（洛氏、布氏） | 23° | ASTM D-785 | 55 | ||
| 剪切强度 | 23° | ASTM D-732 | 600 | kgf/cm2 | |
| 弯曲强度 | -30° | ASTM D-790 | 1600 | kgf/cm2 | |
| 弯曲强度 | 80° | ASTM D-790 | 250 | kgf/cm2 | |
| 弯曲弹性率 | 80° | ASTM D-790 | 7000 | kgf/cm2 | |
| 屈服下的伸张强度 | 80° | ASTM D-638 | 320 | kgf/cm2 | |
| 屈服下的伸张强度 | -30° | ASTM D-638 | 870 | kgf/cm2 | |
| 1%变形下的压缩强度23 | ASTM D-695 | 200 | kgf/cm2 | ||
| 屈服下的伸张强度 | 23° | ASTM D-638 | 400 | kgf/cm2 | |
| 抗冲击强度 | 23° | ASTM D-256 | 5.0 | kgf.cm/cm | |
| 弯曲强度 | 80° | ASTM D-790 | 400 | kgf/cm2 | |
| 弯曲强度 | 23° | ASTM D-790 | 400 | kgf/cm2 | |
| 硬度（洛氏、布氏） | 23° | ASTM D-785 | 120 | ||
| 弯曲弹性率 | -30° | ASTM D-790 | 34000 | kgf/cm2 | |
| 抗冲击强度 | -30° | ASTM D-256 | 3.0 | kgf.cm/cm | |
| 硬度（洛氏、布氏） | 23° | ASTM D-785 | 85 | ||
| 屈服下的延伸率 | 23° | ASTM D-638 | 8 | % | |
| 弯曲强度 | -30° | ASTM D-790 | 1350 | kgf/cm2 | |
| 抗冲击强度 | 23° | ASTM D-256 | 45 | kgf.cm/cm | |
| 断裂下的伸张强度 | 23° | ASTM D-638 | 650 | kgf/cm2 | |
| 硬度（洛氏、布氏） | 23° | ASTM D-785 | 85 | ||
| 屈服下的伸张强度 | -30° | ASTM D-638 | 1100 | kgf/cm2 | |
| 弯曲弹性率 | 80° | ASTM D-790 | 4000 | kgf/cm2 | |
| 1%变形下的压缩强度23 | ASTM D-695 | 100 | kgf/cm2 | ||
| 弯曲强度 | 23° | ASTM D-790 | 1100 | kgf/cm2 | |
| 剪切强度 | 23° | ASTM D-732 | 650 | kgf/cm2 | |
| 屈服下的伸张强度 | 23° | ASTM D-638 | 750 | kgf/cm2 | |
| 弯曲弹性率 | -30° | ASTM D-790 | 36000 | kgf/cm2 | |
| TABER磨耗率 | ASTM D-1044 | 7 | mg | ||
| 弯曲弹性率 | 23° | ASTM D-790 | 26000 | kgf/cm2 | |
| 断裂下的延伸率 | 23° | ASTM D-638 | >200 | % | |
| 断裂下的延伸率 | 23° | ASTM D-638 | 100 | % | |
| 屈服下的伸张强度 | 80° | ASTM D-638 | 180 | kgf/cm2 | |
| 电气性能 | 介电常数 | 60HZ | ASTM D-150 | 9.0 | |
| 介电常数 | 106HZ | ASTM D-150 | 4.5 | ||
| 介电损耗 | 106HZ | ASTM D-150 | 0.12 | ||
| 介电常数 | 106HZ | ASTM D-150 | 3.5 | ||
| 体积电阻率 | ASTM D-257 | 1012 | Ω.cm | ||
| 介电损耗 | 60HZ | ASTM D-150 | 0.10 | ||
| 体积电阻率 | ASTM D-257 | 1015 | Ω.cm | ||
| 抗电弧强度 | ASTM D-495 | 136 | S | ||
| 绝缘耐力 | ASTM D-149 | 20 | KV/mm | ||
| 介电损耗 | 103HZ | ASTM D-150 | 0.10 | ||
| 介电损耗 | 103HZ | ASTM D-150 | 0.02 | ||
| 介电损耗 | 60HZ | ASTM D-150 | 0.01 | ||
| 介电常数 | 103HZ | ASTM D-150 | 8.0 | ||
| IEC电路 | UL-746 | 600 | V | ||
| 介电损耗 | 106HZ | ASTM D-150 | 0.02 | ||
| 介电常数 | 60HZ | ASTM D-150 | 3.9 | ||
| 介电常数 | 103HZ | ASTM D-150 | 3.8 | ||
| 热性能 | 残性热膨胀系数 | ASTM D-696 | 8 | X的10-5cm/cm/°C | |
| 熔点 | DSC | 215-225 | °C | ||
| 热变形温度 | 4.6kgf/cm2 | ASTM D-648 | 175 | °C | |
| 热变形温度 | 18.6kgf/cm2 | ASTM D-648 | 75 | °C | |
| 其它性能 | 吸水率 | ASTM D-570 | 10.7 | % | |
| 成型收缩率 | UBEmethod | 1.4 | % | ||
| 成型收缩率 | UBEmethod | 1.5 | % | ||
| 吸水率 | ASTM D-570 | 1.8 | % | ||
| 燃烧率 | UL-94 | V-2 | |||
| 比重 | ASTM D-792 | 1.14 | |||