| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 物理性能 | 熔体流动速率 | 200℃×5kg | ASTM D-1238 | 3.0 | g/10min | |
| 熔体流动速率 | 220℃×10kg | ISO1133 | 28 | g/10min | ||
| 阻燃性 | File NO.E196075 | 1/16〃HB | ||||
| 比重 | ASTM D-792 | 1.06 | 23/23℃ | |||
| 机械性能 | 引张强度 | ASTM D-638 | 730 | kg/cm2 | ||
| 洛氏硬度 | ASTM D-785 | 83 | M | |||
| 弯曲强度 | ASTM D-790 | 1030 | kg/cm2 | |||
| 弯曲弹性率 | ASTM D-790 | 3.6×104 | kg/cm2 | |||
| 伸长率 | ASTM D-638 | 3.0 | % | |||
| IZOD冲击强度 | 1/8" | ASTM D-256 | 2.0 | kg.cm/cm | ||
| IZOD冲击强度 | 1/4〃 | ASTM D-256 | 1.8 | kg.cm/cm | ||
| 热性能 | 热变形温度 | 未退火 | ASTM D-648 | 92(198) | ℃(℉) | |
| 退火 | ASTM D-648 | 101(214) | ℃(℉) | |||
| 维卡软化点 | ASTM D-1525 | 105(221) | ℃(?H) | |||