原料技术数据
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 物理性能 | 模塑收缩率 | ASTM D-955 | 0.4-0.7 | % | ||
| 比重 | ASTM D-792 | 1.04 | 23/23℃ | |||
| 熔体流动速率 | 200℃ 5kg(条件G) | ASTM D-1238 | 4.5 | g/10min | ||
| 熔体流动速率 | 200℃ 21.6kg | ASTM D-1238 | 50 | g/10min | ||
| 机械性能 | 洛氏硬度 | ASTM D-785 | 108 | R | ||
| 缺口冲击强度 | 23℃ 1/4in(6.4mm) | ASTM D-256 | 23 | kg.cm/cm | ||
| 缺口冲击强度 | 23℃ 1/8in(3.2mm) | ASTM D-256 | 26 | kg.cm/cm | ||
| 弯曲模量 | 23℃ | ASTM D-790 | 24000 | kg/cm2 | ||
| 弯曲强度 | 23℃ | ASTM D-790 | 650 | kg/cm2 | ||
| 伸长率 | ASTM D-638 | 30 | % | |||
| 拉伸强度 | 23℃ | ASTM D-638 | 480 | kg/cm2 | ||
| 热性能 | 维卡软化点 | ASTM D-1525 | 95(203) | ℃(℉) | ||
| 热变形温度 | 未退火 | 6.4mm 18.6kg/cm2 | ASTM D-648 | 85(185) | ℃(℉) | |
| 退火 | 6.4mm 18.6kg/cm2 | ASTM D-648 | 95(203) | ℃(℉) | ||