Asaflex™ 825
苯乙烯-丁二烯-苯乙烯嵌段共聚物
产品说明：
Injection- and blow-molding grade. For transparent products with superior impact strength. Blended with GPPS (general-purpose polystyrene) or SC*, for films with good thermal stability. Capability for profile-extrusion products. It is supplied in pellet form.
Cosmetics caps, stationery goods, other consumer goods. Blended with GPPS for PSP* laminate films and IC magazine rails, and with SC* for shrink films.
* Styrenic copolymer from PS Japan Corp. similar to Asaflex™ 825 in refraction index, resulting in blends that provide sheet transparency significantly higher than attainable with any GPPS.
Asaflex™ 825 物性表
| 基本信息 |
|
| 特性 |
|
| 用途 |
Cosmetic Packaging Water Sports Equipment 薄膜 层压板 文具 消费品应用领域 型材 |
| 外观 |
|
| 形式 |
|
| 加工方法 |
|
| 物理性能 |
额定值 |
单位制 |
测试方法 |
| 密度 |
1.02 |
g/cm3 |
ISO 1183 |
| 熔流率（熔体流动速率） (200°C/5.0 kg) |
6.0 |
g/10 min |
ISO 1133 |
| 收缩率 |
0.20 到 0.80 |
% |
|
| 吸水率 (23°C, 24 hr) |
0.10 |
% |
ISO 62 |
| 硬度 |
额定值 |
单位制 |
测试方法 |
| 洛氏硬度 (R 计秤) |
55 |
|
ISO 2039-2 |
| 肖氏硬度 (邵氏 D) |
71 |
|
ISO 868 |
| 机械性能 |
额定值 |
单位制 |
测试方法 |
| 拉伸应力 (屈服) |
27.0 |
MPa |
ISO 527-2/5 |
| 拉伸应变 (断裂) |
200 |
% |
ISO 527-2/5 |
| 弯曲模量 |
1200 |
MPa |
ISO 178 |
| 弯曲应力 |
37.0 |
MPa |
ISO 178 |
| 冲击性能 |
额定值 |
单位制 |
测试方法 |
| 简支梁缺口冲击强度 (完全断裂) |
2.0 |
kJ/m2 |
ISO 179 |
| 简支梁无缺口冲击强度 (完全断裂) |
100 |
kJ/m2 |
ISO 179 |
| 热性能 |
额定值 |
单位制 |
测试方法 |
| 热变形温度 (1.8 MPa, 未退火) |
57.0 |
°C |
ISO 75-2/A |
| 维卡软化温度 |
82.0 |
°C |
ISO 306/A50 |
| 光学性能 |
额定值 |
单位制 |
测试方法 |
| 透射率 (2000 μm) |
90.0 |
% |
ISO 3537 |
| 雾度 (2000 μm) |
0.50 |
% |
ISO 3537 |