东莞市方德塑胶原料有限公司
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | 1.16 g/cc | 0.0419 lb/in3 | ISO 1183 |
| 吸水率 | 0.80 % @Time 86400 sec |
0.80 % @Time 24.0 hour |
ISO 62 |
| 平衡吸湿 | 2.3 % | 2.3 % | 50% RH; ISO 62 |
| 线性成型收缩率,Flow | 0.012 cm/cm @Diameter 2.00 mm |
0.012 in/in @Diameter 0.0787 in |
ISO 294-4 |
| 线性成型收缩率，横向 | 0.014 cm/cm @Diameter 2.00 mm |
0.014 in/in @Diameter 0.0787 in |
ISO 294-4 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(断裂) | 5.50 MPa | 798 psi | ISO 527-2 |
| 抗张强度(屈服) | 75.0 MPa | 10900 psi | ISO 527-2 |
| 拉伸模量 | 5.00 GPa | 725 ksi | ISO 527-2 |
| 弯曲强度 | 92.0 MPa | 13300 psi | ISO 178 |
| 弯曲模量 | 3.20 GPa | 464 ksi | ISO 178 |
| 泊松比 | 0.40 | 0.40 | ISO 527-2 |
| 悬壁梁缺口冲击强度 | 6.00 kJ/m2 | 2.86 ft-lb/in2 | ISO 180 |
| 简支梁无缺口冲击强度 | NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
ISO 179/1eU |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179/1eU | |
| 简支梁缺口冲击强度 | 0.540 J/cm2 @Temperature -30.0 °C |
2.57 ft-lb/in2 @Temperature -22.0 °F |
ISO 179/1eA |
| 0.540 J/cm2 @Temperature 23.0 °C |
2.57 ft-lb/in2 @Temperature 73.4 °F |
ISO 179/1eA |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 体积电阻率 | 1.00e 11 ohm-cm @Thickness 0.750 mm |
1.00e 11 ohm-cm @Thickness 0.0295 in |
IEC 60093 |
| 介电强度 | 13.0 kV/mm @Thickness 1.00 mm |
330 kV/in @Thickness 0.0394 in |
IEC 60243 |
| 耐电弧性 | 120 - 179 sec @Thickness 3.00 mm |
120 - 179 sec @Thickness 0.118 in |
ASTM D495 |
| 相比耐漏电起痕指数(CTI) | 600 V @Thickness 3.00 mm |
600 V @Thickness 0.118 in |
IEC 60112 |
| 热丝引燃 (HWI) | 7.0 - 14 sec @Thickness 0.400 mm |
7.0 - 14 sec @Thickness 0.0157 in |
UL 746 |
| 7.0 - 14 sec @Thickness 0.750 mm |
7.0 - 14 sec @Thickness 0.0295 in |
UL 746 | |
| 7.0 - 14 sec @Thickness 1.50 mm |
7.0 - 14 sec @Thickness 0.0591 in |
UL 746 | |
| 15 - 29 sec @Thickness 3.00 mm |
15 - 29 sec @Thickness 0.118 in |
UL 746 | |
| 高电弧燃烧指数(HAI) | >= 120 arcs @Thickness 0.400 mm |
>= 120 arcs @Thickness 0.0157 in |
UL 746 |
| >= 120 arcs @Thickness 0.750 mm |
>= 120 arcs @Thickness 0.0295 in |
UL 746 | |
| >= 120 arcs @Thickness 1.50 mm |
>= 120 arcs @Thickness 0.0591 in |
UL 746 | |
| >= 120 arcs @Thickness 3.00 mm |
>= 120 arcs @Thickness 0.118 in |
UL 746 | |
| 高压电弧跟踪率，HVTR | 10.1 - 25.4 mm/min | 0.398 - 1.00 in/min | UL 746 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线形热膨胀系数 - 流动 | 11.0 μm/m-°C @Thickness 2.00 mm, Temperature 23.0 - 55.0 °C |
6.11 μin/in-°F @Thickness 0.0787 in, Temperature 73.4 - 131 °F |
ISO 11359-2 |
| 线性热膨胀系数,横向流动 | 11.0 μm/m-°C @Thickness 2.00 mm, Temperature 23.0 - 55.0 °C |
6.11 μin/in-°F @Thickness 0.0787 in, Temperature 73.4 - 131 °F |
ISO 11359-2 |
| 熔融温度 | 244 °C | 471 °F | ISO 11357-3 |
| 载荷下热变形温度(0.46 MPa) | 225 °C | 437 °F | Unannealed; ISO 75-2/B |
| 载荷下热变形温度(1.8 MPa) | 65.0 °C | 149 °F | Unannealed; ISO 75-2/A |
| UL RTI | 130 °C @Thickness 0.400 mm |
266 °F @Thickness 0.0157 in |
UL 746 |
| 130 °C @Thickness 0.750 mm |
266 °F @Thickness 0.0295 in |
UL 746 | |
| 130 °C @Thickness 1.50 mm |
266 °F @Thickness 0.0591 in |
UL 746 | |
| 130 °C @Thickness 3.00 mm |
266 °F @Thickness 0.118 in |
UL 746 | |
| UL RTI，机械冲击 | 65.0 °C @Thickness 0.400 mm |
149 °F @Thickness 0.0157 in |
UL 746 |
| 65.0 °C @Thickness 0.750 mm |
149 °F @Thickness 0.0295 in |
UL 746 | |
| 85.0 °C @Thickness 1.50 mm |
185 °F @Thickness 0.0591 in |
UL 746 | |
| 85.0 °C @Thickness 3.00 mm |
185 °F @Thickness 0.118 in |
UL 746 | |
| UL RTI，机械无冲击 | 100 °C @Thickness 0.400 mm |
212 °F @Thickness 0.0157 in |
UL 746 |
| 100 °C @Thickness 0.750 mm |
212 °F @Thickness 0.0295 in |
UL 746 | |
| 100 °C @Thickness 1.50 mm |
212 °F @Thickness 0.0591 in |
UL 746 | |
| 110 °C @Thickness 3.00 mm |
230 °F @Thickness 0.118 in |
UL 746 | |
| 可燃性(UL94) | V-0 @Thickness 0.400 mm |
V-0 @Thickness 0.0157 in |
|
| V-0 @Thickness 0.750 mm |
V-0 @Thickness 0.0295 in |
||
| V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
||
| V-0 @Thickness 3.00 mm |
V-0 @Thickness 0.118 in |
||
| 极限氧指数 | 29 % | 29 % | ISO 4589-2 |
| 灼热丝易燃指数 | 725 °C @Thickness 3.00 mm |
1340 °F @Thickness 0.118 in |
Ignition Temperature; IEC 60695-2-13 |
| 775 °C @Thickness 1.50 mm |
1430 °F @Thickness 0.0591 in |
Ignition Temperature; IEC 60695-2-13 | |
| 875 °C @Thickness 0.400 mm |
1610 °F @Thickness 0.0157 in |
Ignition Temperature; IEC 60695-2-13 | |
| 875 °C @Thickness 0.750 mm |
1610 °F @Thickness 0.0295 in |
Ignition Temperature; IEC 60695-2-13 | |
| 960 °C @Thickness 0.400 mm |
1760 °F @Thickness 0.0157 in |
Flammability Index; IEC 60695-2-12 | |
| 960 °C @Thickness 0.750 mm |
1760 °F @Thickness 0.0295 in |
Flammability Index; IEC 60695-2-12 | |
| 960 °C @Thickness 1.50 mm |
1760 °F @Thickness 0.0591 in |
Flammability Index; IEC 60695-2-12 | |
| 960 °C @Thickness 3.00 mm |
1760 °F @Thickness 0.118 in |
Flammability Index; IEC 60695-2-12 |
| 加工性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 料筒后部温度 | 240 - 270 °C | 464 - 518 °F | |
| 料筒中部温度 | 240 - 270 °C | 464 - 518 °F | |
| 料筒前部温度 | 240 - 270 °C | 464 - 518 °F | |
| 射嘴温度 | 240 - 270 °C | 464 - 518 °F | |
| 加工（熔体）温度 | 250 - 270 °C | 482 - 518 °F |