PPA Amodel AT-1001L 产品说明：

Amodel® AT-1001L is an unreinforced, impact modified polyphthalamide (PPA) resin that exhibits exceptional impact strength at temperatures ranging from room temperature to as low as -40°F (-40°C), which suggests possible applications in ski boots and hockey skates.

In addition, its chemical and wear resistance, combined with good mechanical properties, make Amodel® AT-1001L resin a prime candidate for applications such as anti-friction and wear resistant components, chemical, oil field, automotive and safety equipment.

物理性能	额定值	单位制	测试方法
密度	1.11	g/cm3	ISO 1183/A
收缩率			ASTM D955
流动	1.7 到 2.2	%	ASTM D955
横向流动	1.9 到 2.1	%	ASTM D955
吸水率 (24 hr)	0.75	%	ASTM D570

机械性能	额定值	单位制	测试方法
拉伸模量	1900	MPa	ASTM D638
抗张强度 (断裂)	62.1	MPa	ASTM D638
伸长率			ASTM D638
屈服	6.0	%	ASTM D638
断裂	30	%	ASTM D638
弯曲模量	2210	MPa	ASTM D790
弯曲强度	96.5	MPa	ASTM D790
泊松比	0.35		ASTM E132

冲击性能	额定值	单位制	测试方法
悬壁梁缺口冲击强度			ASTM D256
-40°C	750	J/m	ASTM D256
23°C	1100	J/m	ASTM D256

PPA Amodel AT-1001L

PPA (Polyphthalamide ) 聚邻苯二甲酰胺，在高温高湿状态下，PPA的抗拉强度比尼龙6高20%，比尼龙66更高；PPA材料的弯曲模量比尼龙高20%，硬度更大，能抗长时间的拉伸蠕变；且PPA的耐汽油、耐油脂和冷却剂的能力也比PA强；一种耐高温尼龙，这种材料可以耐200℃的持续高温，并且还能保持良好的尺寸稳定性 [1]  。

聚邻苯二甲酰胺（简称PPA）树脂是以对苯二甲酸或间苯二甲酸为原料的半芳香族聚酰胺。既有半结晶态的，也有非结晶态的，其玻璃化温度在255°F左右。非结晶态的PPA主要用于要求阻隔性能的场合；半结晶态的PPA树脂主要用于注塑加工，也用于其它熔融加工工艺。下文主要介绍后者——半结晶态PPA树脂，特别注明的除外。半结晶态PPAS的熔点约为590°F，以不透明矩形切片的形式供应。

聚邻苯二酰胺（简称PPA）树脂是以对苯二甲酸或邻苯二甲酸为原料的半芳香族聚酰胺。既有半结晶态的，也有非结晶态的，其玻璃化温度在255°F左右。非结晶态的PPA主要用于要求阻隔性能的场合；半结晶态的PPA树脂主要用于注塑加工，也用于其它熔融加工工艺下文主要介绍后者——半结晶态PPA树脂，特别注明的除外。半结晶态PPAS的熔点约590°F，以不透明矩形切片的形式供应。

PPA塑胶原料

:PPA荷兰DSM物性 PPA美国阿莫科物性 PPA瑞士EMS物性

(3)PPA 美阿莫科 AF-4122NL 22%玻纤增强、高光学反射能力90%以上

(4)PPA 美国阿莫科AF-1130VO 33%玻纤强化、耐高温300℃ 、良好韧性、阻燃UL94V0

(5)PPA 美国阿莫科AS-1133HS 33%玻纤强化、良好韧性、阻燃UL94HB

(6)PPA AF-4133V0 33%玻纤强化、热变形温300℃ 、良好加工性能、阻燃UL94V0

(7)PPA AF-6133V0 玻纤增强33%、适合用于红外照射和潮湿环境

(8)PPA A-1006 良好耐冲击性能、适合做承受压力的管状接头、水龙头等

(9)PPA AS-1566HS 65%矿物玻纤强化、高温高弯曲强度和硬度、可着色

PPA Amodel AT-1001L 可提供COA、COC,ROHS.MSDS.UL黄卡等等资料，价格最优，质量保证！