PEEK KETASPIRE KT-880 GF30 产品说明:
KetaSpire® KT-880 GF30 is the high-flow, 30% glass-fiber reinforced grade of polyetheretherketone (PEEK). This resin offers higher strength and stiffness properties relative to unreinforced KetaSpire® PEEK resin. Reinforcement also affords greater mechanical robustness in structural applications, particularly those with service temperatures approaching 300°C.
KetaSpire® PEEK is produced to the highest industry standards and is characterized by a distinct combination of properties, which include excellent wear resistance, best-in-class fatigue resistance, ease of melt processing, high purity and excellent chemical resistance to organics, acids and bases.
These properties make it well-suited for applications in healthcare, transportation, electronics, chemical processing and other industrial uses.
物理性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
比重 |
1.53 |
1.53 |
g/cm3 |
ASTM D792 |
熔流率(熔体流动速率) (400°C/2.16 kg) |
14 |
14 |
g/10 min |
ASTM D1238 |
收缩率 1 |
|
|
|
ASTM D955 |
流动 : 3.18 mm |
0.10 到 0.30 |
0.10 到 0.30 |
% |
ASTM D955 |
横向流动 : 3.18 mm |
1.3 到 1.5 |
1.3 到 1.5 |
% |
ASTM D955 |
吸水率 (24 hr) |
0.10 |
0.10 |
% |
ASTM D570 |
硬度 |
干燥 |
调节后的 |
单位制 |
测试方法 |
洛氏硬度 (M 级) |
105 |
105 |
|
ASTM D785 |
机械性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
拉伸模量 |
|
|
|
|
-- 2 |
10800 |
10800 |
MPa |
ASTM D638 |
-- |
11200 |
11200 |
MPa |
ISO 527-2/1A/1 |
拉伸应力 |
|
|
|
|
屈服 |
174 |
174 |
MPa |
ISO 527-2/1A/5 |
-- |
162 |
162 |
MPa |
ASTM D638 |
伸长率 |
|
|
|
|
断裂 |
2.8 |
2.8 |
% |
ASTM D638 |
断裂 |
2.8 |
2.8 |
% |
ISO 527-2/1A/5 |
弯曲模量 |
|
|
|
|
-- |
10500 |
10500 |
MPa |
ASTM D790 |
-- |
10600 |
10600 |
MPa |
ISO 178 |
弯曲强度 |
|
|
|
|
-- |
260 |
260 |
MPa |
ASTM D790 |
-- |
239 |
239 |
MPa |
ISO 178 |
压缩强度 |
183 |
183 |
MPa |
ASTM D695 |
剪切强度 |
94.4 |
94.4 |
MPa |
ASTM D732 |
PEEK KETASPIRE KT-880 GF30 可提供COA、COC,ROHS.MSDS.UL黄卡等等资料,价格最优,质量保证!