POM HOSTAFORM C 9021 G 产品说明：

Chemical abbreviation according to ISO 1043-1: POM
Molding compound ISO 9988- POM-K, M-GNS, 02-002

POM copolymer

Injection molding type with (R) GUR (PE-UHMW) modified; good
chemical resistance to solvents, fuel and strong alkalis as well as
good hydrolysis resistance; high resistance to thermal and oxidative
degradation.

Burning rate ISO 3795 and FMVSS 302 < 100 mm/min for a thickness
more than 1 mm.

Ranges of applications: for parts under abrasion stress.

FMVSS = Federal Motor Vehicle Safety Standard (USA)

物理性能	额定值	单位制	测试方法
密度	1.34	g/cm3	ISO 1183
溶化体积流率（MVR） (190°C/2.16 kg)	5.50	cm3/10min	ISO 1133
收缩率			ISO 294-4
垂直流动方向	1.8	%	ISO 294-4
流动方向	2.3	%	ISO 294-4
吸水率 (饱和, 23°C)	0.80	%	ISO 62

机械性能	额定值	单位制	测试方法
拉伸模量	2300	MPa	ISO 527-2/1A/1
拉伸应力 (屈服)	45.0	MPa	ISO 527-2/1A/50
拉伸应变 (屈服)	9.0	%	ISO 527-2/1A/50
标称拉伸断裂应变	10	%	ISO 527-2/1A/50
拉伸蠕变模量			ISO 899-1
1 hr	2000	MPa	ISO 899-1
1000 hr	1300	MPa	ISO 899-1
弯曲模量 (23°C)	2100	MPa	ISO 178

POM HOSTAFORM C 9021 G

POM应用

.可代替大部分有色金属、汽车、机床、仪表内件、轴承、紧固件、齿轮、弹簧片、管道、运输带配件、电水煲、泵壳、沥水器、水龙头等.

一般性能

（1）POM是结晶型塑料,密度为1.42g/cm3,它的钢性很好,俗称“赛钢”.

（2）它具有耐疲劳、耐蠕变、耐磨、耐热、耐冲击等优良的性能,且摩擦系数小,自润滑性好.

（3）POM不易吸湿,吸水率为0.22～0.25%,在潮湿的环境中尺寸稳定性好,其收缩率为2.1%(较大),注塑时尺寸较难控制,热变形温度为172℃,聚甲醛有均聚甲醛两种,性能不同(均聚甲醛耐温性好一点).

力学性能

POM强度、刚度高，弹性好，减磨耐磨性好。其力学性能优异，比强度可达50.5MPa，比刚度可达2650MPa，与金属十分接近。POM的力学性能随温度变化小，共聚POM比均聚POM的变化稍大一点。POM的冲击强度较高，但常规冲击不及ABS和PC；POM对缺口敏感，有缺口可使冲击强度下降90%之多。POM的疲劳强度十分突出，10交变载荷作用后，疲劳强度可达35MPa，而PA和PC仅为28MPa。POM的蠕变性与PA相似，在20℃、21MPa、3000h时仅为2.3%，而且受温度的影响很小。POM的摩擦因数小，耐磨性好（POM>PA66>PA6>ABS>HPVC>PS>PC），极限PV值很大，自润滑性好。POM制品对磨时，高载荷作用时易产生类似尖叫的噪声。

电学性能

POM的电绝缘性较好，几乎不受温度和湿度的影响；介电常数和介电损耗在很宽的温度、湿度和频率范围内变化很小；耐电弧性极好，并可在高温下保持。POM的介电强度与厚度有关，厚度0.127mm时为82.7kV/mm，厚度为1.88mm时为23.6kV/mm。

POM环境性能

POM不耐强碱和氧化剂，对烯酸及弱酸有一定的稳定性。POM的耐溶剂性良好，可耐烃类、醇类、醛类、醚类、汽油、润滑油及弱碱等，并可在高温下保持相当的化学稳定性。吸水性小，尺寸稳定性好。

POM HOSTAFORM C 9021 G 可提供COA、COC,ROHS.MSDS.UL黄卡等等资料，价格最优，质量保证！