东莞市恒磊塑胶有限公司
PBT LNP LUBRICOMP WFL34 产品说明：
LNP LUBRICOMP* WFL34 is a compound based on PBT resin containing 20% Glass Fiber, 15% PTFE. Added feature of this grade is: Wear Resistant.
Also known as: LNP* LUBRICOMP* Compound WFL-4034
Product reorder name: WFL34
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 比重 | 1.58 | g/cm3 | ASTM D792, ISO 1183 |
| 收缩率 | ASTM D955 | ||
| 流动 : 24小时 | 0.30 到 0.50 | % | ASTM D955 |
| 横向流动 : 24小时 | 1.0 到 3.0 | % | ASTM D955 |
| 吸水率 | |||
| 24 hr, 50% RH | 0.054 | % | ASTM D570 |
| 平衡, 23°C, 50% RH | 0.072 | % | ISO 62 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 拉伸模量 | |||
| -- 1 | 8270 | MPa | ASTM D638 |
| -- | 7890 | MPa | ISO 527-2/1 |
| 抗张强度 | |||
| 屈服 2 | 118 | MPa | ASTM D638 |
| 屈服 | 114 | MPa | ISO 527-2/5 |
| 断裂 3 | 118 | MPa | ASTM D638 |
| 断裂 | 114 | MPa | ISO 527-2/5 |
| 伸长率 | |||
| 屈服 4 | 2.6 | % | ASTM D638 |
| 屈服 | 2.6 | % | ISO 527-2/5 |
| 断裂 5 | 2.6 | % | ASTM D638 |
| 断裂 | 2.6 | % | ISO 527-2/5 |