PPS FORTRON MT9320C0 产品说明：

Fortron MT9320C0 is an unfilled grade used for extrusion applications. It demonstrates excellent chemical resistance and thermal stability as well as a high melt strength. Components made of this grade may be used for medical, dental, pharmaceutical, and certain food handling applications. Fortron MT9320C0 is in compliance with ISO 10993, USP Class VI and it is included in the Fortron Drug and Device Master Files at the FDA. This grade complies with the FDA Food Contact Notification (FCN-No. 40) for repeat-use applications.

物理性能	额定值	单位制	测试方法
密度	1.35	g/cm3	ISO 1183
吸水率 (饱和, 23°C)	0.020	%	ISO 62

机械性能	额定值	单位制	测试方法
拉伸应力 (断裂)	85.0	MPa	ISO 527-2/1A/5
拉伸应变 (断裂)	6.0	%	ISO 527-2/1A/5
弯曲模量 (23°C)	4200	MPa	ISO 178
弯曲应力 (23°C)	140	MPa	ISO 178

冲击性能	额定值	单位制	测试方法
悬壁梁缺口冲击强度 (23°C)	3.5	kJ/m2	ISO 180/1A

热性能	额定值	单位制	测试方法
热变形温度
1.8 MPa, 未退火	115	°C	ISO 75-2/A
8.0 MPa, 未退火	95.0	°C	ISO 75-2/C
玻璃转化温度 1	90.0	°C	ISO 11357-2
熔融温度 2	280	°C	ISO 11357-3

PPS FORTRON MT9320C0 可提供COA、COC,ROHS.MSDS.UL黄卡等等资料，价格最优，质量保证！

加工特性

树脂厂商提供的PPS为一种相对质量比较低（4000~5000）、结晶度较高（75%）的白色粉末，这种纯PPS无法直接塑化成型，只能用于喷涂。用于塑化成型的PPS，必须进行交联改性处理，使熔体的粘度上升。一般交联后的熔融指数达到10~20为宜；进行玻璃纤维增强PPS的熔融指数可大一些，但不能大于200。

（1）注塑：可采用通用注塑机，玻璃纤维增强PPS的熔融指数以50为宜。注塑的工艺条件为：料筒温度，纯PPS为280~330℃，40%GFPPS为300-350℃；喷嘴温度，纯PPS为305℃，40%GFPPS为330℃；模具温度120-180℃；注塑压力，50-130MPA。

（2）挤出：采用排气式挤出机，工艺为：加料段温度小于200℃；料筒温度300-340℃，连接体温度320-340℃，口模温度300-320℃。

（3）模压成型：适合大型制品，采用两次压缩，先冷却，后热压。热压的预热温度纯PPS为360℃左右15min,GFPPS为380℃左右20min;模压压力为10~30Mpa，冷却到150℃脱模。

（4）喷涂成型：采用悬浮喷涂法和悬浮喷涂与干粉热喷混合法，都是将PPS喷涂到金属表面，再经过塑化、淬火处理而得到涂层；PPS的涂层处理温度在300℃以上，保温30min。

PPS的应用：

机械工业：机械工业中特别运用于在高湿、强腐蚀的环境下的部件制备。用于壳体、结构件、耐磨件及密封材料，具体有如：泵壳、泵轮、阀、轴承、轴承支架、活塞环及齿轮、滑轮、风扇、流量计部件、法兰盘、万向头、计数器、水准仪等。