SABIC PP 518A 产品说明：
Provisional - PP Homopolymer for fiber applications
PP 518A is a PP homopolymer with broad molecular weight distribution intended for fiber extrusion applications.
PP 518A has following features:
Consistent processability
Good thread line stability
Good gas fading resistance
Typical Applications
PP 518A is particularly suitable for producing bulk continuous filament (BCF), continuous filament (CF) and staple fiber yarns for carpet pile and upholstery.
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 比重 1 | 0.905 | g/cm3 | ASTM D792 |
| 熔流率（熔体流动速率） (230°C/2.16 kg) | 25 | g/10 min | ASTM D1238 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 洛氏硬度 (R 级, 注塑) | 100 | ASTM D785 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 抗张强度 (屈服, 注塑) | 32.0 | MPa | ASTM D638 |
| 伸长率 (屈服, 注塑) | 12 | % | ASTM D638 |
| 弯曲模量 - 1% 正割 (注塑) | 1550 | MPa | ASTM D790A |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 悬壁梁缺口冲击强度 (23°C, 注塑) | 30 | J/m | ASTM D256 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 载荷下热变形温度 (0.45 MPa, 未退火) | 118 | °C | ASTM D648 |
| 维卡软化温度 | 152 | °C | ASTM D1525 2 |
SABIC PP 518A
甲基排列在分子主链的同一侧称等规聚丙烯，若甲基无秩序的排列在分子主链的两侧称无规聚丙烯，当甲基交替排列在分子主链的两侧称间规聚丙烯。一般工业生产的聚丙烯树脂中，等规结构含量约为95%，其余为无规或间规聚丙烯。工业产品以等规物为主要成分。聚丙烯也包括丙烯与少量乙烯的共聚物在内。通常为半透明无色固体，无臭无毒。由于结构规整而高度结晶化，故熔点可高达167℃。耐热、耐腐蚀，制品可用蒸汽消毒是其突出优点。密度小，是最轻的通用塑料。缺点是耐低温冲击性差，较易老化，但可分别通过改性予以克服。
一、均聚PP-聚丙烯 [size=-1]Homo-polymer polypropylene，简称PPH聚丙烯PP的均聚物简称PPH，是单一丙烯单体的聚合物。聚丙烯（PP）作为热塑塑料聚合物于1957年开始商品化生产，是有规立构聚合物中的第一个。其历史意义更体现在，它一直是增长最快的主要热塑性塑料，2004年它的全国总产量达到300万吨。它在热塑性塑料领域内有十分广泛的应用，特别是在纤维和长丝、薄膜挤压、注塑加工等方面。
二、PP共聚物，Polypropylene Copolymer， 简称PPC，是丙烯单体与乙烯单体的共聚物；按照乙烯单体在分子链上的分布方式，共聚PP可以分为无规共聚物（PPR）和嵌段共聚物（PPB）两种。PPR的刚性好，但耐冲击性不好，尤其耐低温冲击性更不好，耐蠕变性差。PPB的耐冲击性好，但耐蠕变性和PPR一样差。PPR的耐冲击性和耐蠕变性则都不好。