PS TOTAL Polystyrene rePS-5 产品说明：

TOTAL Petrochemicals rePS-5 is a high heat crystal polystyrene that contains a minimum of 25% recycled polystyrene. The polymer was developed to have properties similar to TOTAL Petrochemicals 585 for use in tandem extrusion foam and injection molded applications.

Applications

• Foam Foodservice Packaging

• Cutlery, Housewares, Office Supplies

General Information

• This polystyrene material complies with FDA food contact regulations as set forth in 21 CFR §177.1640.

• Material Safety Data Sheets are available to help customers satisfy their safety needs.

物理性能	额定值	单位制	测试方法
密度	1.04	g/cm3
熔流率（熔体流动速率） (200°C/5.0 kg)	3.0	g/10 min	ASTM D1238
收缩率 - 流动	0.40 到 0.70	%	ASTM D955
湿度		%

机械性能	额定值	单位制	测试方法
拉伸模量	2900	MPa	ASTM D638
抗张强度	52.4	MPa	ASTM D638
弯曲模量	3380	MPa	ASTM D790
弯曲强度	105	MPa	ASTM D790

热性能	额定值	单位制	测试方法
载荷下热变形温度 (0.45 MPa, 退火)	99.4	°C	ASTM D648
维卡软化温度	107	°C	ASTM D1525

PS TOTAL Polystyrene rePS-5

用途

PS被广泛应用于光学工业中，这是因为它有良好的透光性所致，可制造光学玻璃和光学仪器，也可制作透明或颜色鲜艳的，诸如灯罩、照明器具等。PS还可制作诸多在高频环境中工作的电气元器件和仪表等。由于PS塑料属于难惰性表面材料，工业中贴合，需要使用专业PS胶水粘接。

单独使用PS作制品，脆性大，而在PS中加入少量其他物质，如丁二烯即可明显降低脆性，提高冲击韧性，这种塑料叫抗冲击PS，它的力学性能大为提高，可用此塑料制作出许多性能优良的机械零件和构件来。

物料性能

电绝缘性（尤其高频绝缘性）优良，无色透明，透光率仅次于有机玻璃，着色性耐水性，化学稳定性良好，强度一般，但质脆，易产生应力脆裂，不耐苯、汽油等有机溶剂.适于制作绝缘透明件.装饰件及化学仪器.光学仪器等零件.

成型性能

⒈无定形料，吸湿小，不须充分干燥，不易分解，但热膨胀系数大，易产生内应力.流动性较好，可用螺杆或柱塞式注射机成型.

⒉宜用高料温，高模温，低注射压力，延长注射时间有利于降低内应力，防止缩孔.变形.

⒊可用各种形式浇口，浇口与塑件圆弧连接，以免去处浇口时损坏塑件.脱模斜度大，顶出均匀.塑件壁厚均匀，最好不带镶件，如有镶件应预热.

PS TOTAL Polystyrene rePS-5 可提供COA、COC,ROHS.MSDS.UL黄卡等等资料，价格最优，质量保证！