PC CALIBRE 5201-12 产品说明：

CALIBRE™ 5201-12 polycarbonate resin is 20% glass reinforced containing mold release for optimal processing. This resin exhibits high modulus and excellent dimensional stability. CALIBRE 5201-12 resin is typically used in medical market applications. CALIBRE 5201-12 resin has undergone biocompatibility testing based on ISO 10993 (Biological Evaluation of Medical Devices) and is suitable for use in approved medical applications.

物理性能	额定值	单位制	测试方法
比重	1.36	g/cm3	ASTM D792, ISO 1183/B
熔流率（熔体流动速率） (300°C/1.2 kg)	12	g/10 min	ASTM D1238, ISO 1133
收缩率
流动	0.20 到 0.40	%	ASTM D955
流动方向	0.20 到 0.40	%	ISO 294-4

硬度	额定值	单位制	测试方法
洛氏硬度 (R 级)	122		ASTM D785

机械性能	额定值	单位制	测试方法
拉伸模量
-- 1	5170	MPa	ASTM D638
--	5170	MPa	ISO 527-2/50
抗张强度
屈服 2	82.7	MPa	ASTM D638
屈服	82.7	MPa	ISO 527-2/50
断裂 3	82.7	MPa	ASTM D638
断裂	82.7	MPa	ISO 527-2/50
伸长率
屈服 4	2.6	%	ASTM D638
屈服	2.6	%	ISO 527-2/50
断裂 5	3.0	%	ASTM D638
断裂	2.6	%	ISO 527-2/50
弯曲模量
-- 6	4830	MPa	ASTM D790
-- 7	4820	MPa	ISO 178

PC CALIBRE 5201-12

塑料的处理

PC塑胶原料的吸水率较大，加工前一定要预热干燥，纯PC干燥120℃，改性PC一般用110℃温度干燥4小时以上。干燥时间不能超过10小时。一般可用对空挤出法判断干燥是否足够。再生料的使用比例可达20%。在某些情况下，可100%的使用再生料，实际份量要视制品的品质要求而定。再生料不能同时混合不同的色母粒，否则会严重损坏成品的性质。

注塑机选用

PC塑料制品由于成本及其它方面的原因，多用改性材料，特别是电工产品，还须增加防火性能，在阻燃的PC和其它塑料合金产品成型时，对注塑机塑化系统的要求是混合好、耐腐蚀，常规的塑化螺杆难以做到，在选购时，一定要预先说明。

原料

PC塑料很多用改性材料

Bayer聚碳酸酯总体：

聚碳酸酯其结构可分为脂肪族、芳香族、脂肪族-芳香族等多类品种。

RoHS合规性:RoHS合规；

添加剂:紫外线稳定剂；

外观:清晰/透明；

形式:颗粒料；

性能特点:良好的流动性;脱模性能良好;

粘度，高；光学透明性好、抗冲击强度高；

并具有优异的热安稳性、耐蠕变性、抗寒性、电绝缘性和阻燃性等。

加工方法:薄膜挤出；吹塑成型；挤出成型；热成型；树脂传递成型；涂层；砑光；注射成型也是最重要的加工方法之一；

用途:在透明建筑板材、电子电器、光盘、汽车工业、机械、光学、医药等领域得到广泛运用。

PC塑料物理性能以及加工

低温-45度聚碳酸酯无色透明，耐热，抗冲击，阻燃BI级，在普通运用温度内都有出色的机械功用。

PC CALIBRE 5201-12 可提供COA、COC,ROHS.MSDS.UL黄卡等等资料，价格最优，质量保证！