PC CALIBRE 200-15
| Material Notes: | CALIBRE® 200-15 Polycarbonate resins produced in to compliance with the applicable FDA and European regulations governing food contact. They provide excellent impact resistance, heat distortion resistance and optical clarity. CALIBRE 200-15 series products are available in 4 additive packages: CALIBRE 200: No mold release or UV stabilizer. CALIBRE 201: Mold release. CALIBRE 202: UV Stabilizer. CALIBRE 203: Mold release and UV stabilizer. (Note that CALIBRE 202 and 203 grades are not available in Europe and do not comply with EU food contact regulations). Govt. and Industry Standards:
|
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in3 | ASTM D792 |
| Water Absorption | 0.15 % | 0.15 % | ISO 62 |
| Moisture Absorption at Equilibrium | 0.32 % | 0.32 % | ASTM D570 |
| Linear Mold Shrinkage | 0.00500 - 0.00700 cm/cm | 0.00500 - 0.00700 in/in | Flow; ISO 294-4 |
| Melt Flow | 15 g/10 min @Load 1.20 kg, Temperature 300 °C |
15 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 72 | 72 | ASTM D785 |
| Hardness, Rockwell R | 118 | 118 | ASTM D785 |
| Tensile Strength, Ultimate | 71.0 MPa | 10300 psi | 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 62.1 MPa | 9010 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 150 % | 150 % | 50 mm/min; ASTM D638 |
| Elongation at Yield | 6.0 % | 6.0 % | 50 mm/min; ASTM D638 |
| Tensile Modulus | 2.34 GPa | 339 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 96.5 MPa | 14000 psi | Mehotd I (3 point load), 2 mm/min; ASTM D790 |
| 97.0 MPa | 14100 psi | 2 mm/min; ASTM D790 | |
| Flexural Modulus | 2.40 GPa | 348 ksi | 2 mm/min; ASTM D790 |
| 2.41 GPa | 350 ksi | Mehotd I (3 point load), 2 mm/min; ASTM D790 | |
| Izod Impact, Notched | 8.50 J/cm | 15.9 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | NB | NB | ASTM D256 |
| Izod Impact, Notched (ISO) | 83.0 kJ/m2 | 39.5 ft-lb/in2 | ISO 180/A |
| Tensile Impact Strength | 462 kJ/m2 | 220 ft-lb/in2 | ASTM D1822 |
| Instrumented Impact Total Energy | 87.0 J @Temperature 23.0 °C |
64.2 ft-lb @Temperature 73.4 °F |
3.39 m/sec; ASTM D3763 |
| Abrasion | 45 | 45 | [%], Taber; ASTM D1044 |