东莞市恒磊塑胶有限公司
PC+ABS CYCOLOY CX2244ME 产品说明：
CYCOLOY CX2244ME resin is a flame retardant PC/ABS blend featuring excellent balance of flow and impact together with UL-94 V0 rating at < 1mm. CYCOLOY CX2244ME resin also demonstrates improved chemical resistance to general hospital cleaners which can be considered for healthcare enclosure applications.
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 比重 | |||
| -- | 1.19 | g/cm3 | ASTM D792 |
| -- | 1.20 | g/cm3 | ISO 1183 |
| 熔流率（熔体流动速率） (260°C/2.16 kg) | 18 | g/10 min | ASTM D1238 |
| 溶化体积流率（MVR） (260°C/2.16 kg) | 15.0 | cm3/10min | ISO 1133 |
| 收缩率 - 流动 (3.20 mm) | 0.40 到 0.60 | % | 内部方法 |
| 吸水率 | ISO 62 | ||
| 饱和, 23°C | 0.20 | % | ISO 62 |
| 平衡, 23°C, 50% RH | 0.10 | % | ISO 62 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 拉伸模量 | |||
| -- 1 | 2600 | MPa | ASTM D638 |
| -- | 2600 | MPa | ISO 527-2/1 |
| 抗张强度 | |||
| 屈服 2 | 65.0 | MPa | ASTM D638 |
| 屈服 | 65.0 | MPa | ISO 527-2/50 |
| 断裂 3 | 58.0 | MPa | ASTM D638 |
| 断裂 | 50.0 | MPa | ISO 527-2/50 |
| 伸长率 | |||
| 屈服 4 | 4.1 | % | ASTM D638 |
| 屈服 | 4.0 | % | ISO 527-2/50 |
| 断裂 5 | 100 | % | ASTM D638 |
| 断裂 | 90 | % | ISO 527-2/50 |
PC+ABS CYCOLOY CX2244ME
特点
PC/ABS是一种通过混炼后合成的改性工程塑料。其中，PC就是聚碳酸脂，ABS就是丙烯腈（A）、丁二烯（B）和苯乙 烯（S）的共聚物。这种改性塑料比单纯的PC和ABS性能更好，例如：抗冲击性提高，耐热性提高，硬度提高等等。ABS塑料
特点：
1、综合性能较好,冲击强度较高,化学稳定性,电性能良好.
2、与372有机玻璃的熔接性良好,制成双色塑件,且可表面镀铬,喷漆处理.
3、有高抗冲、高耐热、阻燃、增强、透明等级别。
4、流动性比HIPS差一点，比PMMA、PC等好，柔韧性好。
5、机械性能的卓越平衡
6、低温时也具备高冲击强度
7、室内紫外线稳定性
8、较高的热变形温度（80～125℃）
9、耐燃性（UL945VB）
10、色彩范围广泛
11、 易于注塑和挤塑，吹塑加工
12、良好的电镀性
13、一般密度在1.05-1.20间
鉴别方法
1.新方法：用乙酸乙酯擦，ABS不起丝，HIPS会起丝，但只是指纯的。
2.常用方法：ABS，PS的识别方法有很多种，就ABS而言，表面亮度好，韧性优于PS，火烧后表面会有密密麻麻的小孔，气味有淡淡的甜味；PS又分GPPS，HIPS，EPS三种，较脆，透明的产品较多，HIPS的亮度一般，韧性比ABS要逊色一点，火烧后表面光亮，有苯乙烯的味道。HIPS的截断面发白，但GPPS没有，EPS主要用于泡沫。
电视机壳料而言，有ABS，HIPS之分，一般要根据表面特征，物理特征来区分，表面的亮度好的一般是ABS，用钳子掰时ABS要优于HIPS ，其硬度较高，需要力度大一些，然后根据火焰与味道来区分。