COC TOPAS 6015S-04 产品说明：

Product Description
TOPAS 6015S-04 is a general purpose injection molding grade. It is a glass-clear amorphous polymer with outstanding moisture barrier, chemical resistance, high purity and a non-reactive surface making it an excellent choice for optics, healthcare and other high-tech products. Lower leachables and extractables of TOPAS COC preserve food and drug stability and quality. It is a non-polar substrate that does not promote adsorption, denaturation, aggregation, or precipitation like glass can. This grade has a high (150°C) heat distortion temperature to withstand 121°C and 134°C steam and dry heat sterilization protocols, as well as gamma and EtO procedures.

物理性能	额定值	单位制	测试方法
密度	1.02	g/cm3	ISO 1183
熔流率（熔体流动速率） (260°C/2.16 kg)	3.7	g/10 min	ISO 1133
溶化体积流率（MVR） (260°C/2.16 kg)	4.00	cm3/10min	ISO 1133
收缩率 1	0.50 到 0.70	%	内部方法
吸水率 (饱和, 23°C)	0.010	%	ISO 62

机械性能	额定值	单位制	测试方法
拉伸模量	3000	MPa	ISO 527-2/1A/1
拉伸应力 (屈服)	60.0	MPa	ISO 527-2/1A/50
拉伸应变 (屈服)	2.5	%	ISO 527-2/1A/50

冲击性能	额定值	单位制	测试方法
简支梁缺口冲击强度 (23°C)	1.6	kJ/m2	ISO 179/1eA
简支梁无缺口冲击强度 (23°C)	15	kJ/m2	ISO 179/1eU

热性能	额定值	单位制	测试方法
热变形温度 (0.45 MPa, 未退火)	150	°C	ISO 75-2/B
玻璃转化温度	158	°C	ISO 11357-2
维卡软化温度	156	°C	ISO 306/B50

COC TOPAS 6015S-04

COC产品说明

TOPAS 6017S-04注塑级，具有较高的热变形温度（170°C）和卓越的尺寸稳定性。这是一个玻璃透明无定形聚合物，具有优异的防潮，耐化学性，高纯度的非反应性表面，使它成为一个很好的选择精密光学，医疗保健和其他高科技产品。TOPAS COC下的溶出物和萃取物的保存食物和药物的稳定性和质量。它是一种非极性基材，不促进吸附，聚合，变性，或像玻璃可以沉淀。该牌号具有优良的耐热性，可承受121°C和134°C蒸汽和干热灭菌协议，以及伽马射线和环氧乙烷程序选定的应用程序。

特性：

1) 密度小，比PMMA和PC约低10%，有利于制品轻量化；

 

(2) 饱和吸水率小，Arton吸水率远低于PMMA，不会产生因吸水导致物性下降的影响，Zeonex，Zeonor和Apel则几乎不吸水；

 

(3) 由于含有极性和异向性小的单体，因而为非晶型透明材料，双折射率小；

 

(4) 属高耐热性透明树脂玻璃化温度达140~170℃，玻璃化

 

温度是非晶型聚合物的耐热性指标；

 

(5) 容易注射成型；

 

(6) 机械性能优良，拉伸强度，弹性模量比PC高；

 

(7) 优良的复制性，故制品质量高；

 

(8) 介电常数低，特别是高频性能好，是热塑性塑料中介电性能最好的材料；

 

(9) 耐擦伤性良好，　

 

(10) 与无机、有机材料粘接性好，易于密封；

 

(11) 适合半导体和医疗器械要求；

 

(12) 耐化学药品性、耐酸性、耐碱性优良；

 

(13) 几乎不透水蒸汽，符合同时要求防湿的应用要求。

COC TOPAS 6015S-04 可提供COA、COC,ROHS.MSDS.UL黄卡等等资料，价格最优，质量保证！