美国首诺PA66 VYDYNE 66B 产品说明：
Vydyne 66B is a high-viscosity PA66 resin suitable for injection-molding and extrusion applications. It is available in natural color only. Vydyne 66B resin offers high strength, rigidity and toughness over a broad range of demanding applications and good fluid resistance to a wide variety of chemicals, solvents and oils.
Typical Applications/End Uses:
Typical uses include packaging films, monofilaments, bristles, rods, tubing, sheet and extruded profiles.
| 物理性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
|---|---|---|---|---|
| 密度 | 1.14 | -- | g/cm3 | ISO 1183 |
| 收缩率 | ISO 294-4 | |||
| 垂直流动方向 : 2.00 mm | 2.0 | -- | % | ISO 294-4 |
| 流动方向 : 2.00 mm | 2.1 | -- | % | ISO 294-4 |
| 吸水率 | ISO 62 | |||
| 饱和, 23°C | 8.5 | -- | % | ISO 62 |
| 平衡, 23°C, 50% RH | 2.5 | -- | % | ISO 62 |
| 机械性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
|---|---|---|---|---|
| 拉伸模量 (23°C) | 2800 | 1800 | MPa | ISO 527-2/1A |
| 拉伸应力 | ISO 527-2/1A | |||
| 屈服, 23°C | 85.0 | 55.0 | MPa | ISO 527-2/1A |
| 断裂, 23°C | 55.0 | 70.0 | MPa | ISO 527-2/1A |
| 拉伸应变 (屈服, 23°C) | 5.0 | 20 | % | ISO 527-2 |
| 标称拉伸断裂应变 (23°C) | > 25 | > 150 | % | ISO 527-2/1A |
| 弯曲模量 (23°C) | 3100 | 900 | MPa | ISO 178 |
| 弯曲应力 (23°C) | 90.0 | 30.0 | MPa | ISO 178 |
| 泊松比 (23°C) | 0.42 | -- | ISO 527-2 |
美国首诺PA66 VYDYNE 66B
尼龙中的主要品种是尼龙6和尼龙66，占绝对主导地位，尼龙6为聚己内酰胺，而尼龙66为聚己二酸己二胺，尼龙66比尼龙6要硬l2%；其次是尼龙11，尼龙12，尼龙610，尼龙612，另外还有尼龙1010、尼龙46、尼龙7、尼龙9、尼龙13，新品种有尼龙6I、尼龙9T和特殊尼龙MXD6（阻隔性树脂）等，尼龙的改性品种数量繁多，如增强尼龙、单体浇铸尼龙（MC尼龙）、反应注射成型(RIM)尼龙、芳香族尼龙、透明尼龙、高抗冲（超韧）尼龙、电镀尼龙、导电尼龙、阻燃尼龙，尼龙与其他聚合物共混物和合金等，满足不同特殊要求，广泛用作金属，木材等传统材料代用品。
PA特性
尼龙作为大用量的工程塑料，广泛用于机械、汽车、电器、纺织器材、化工设备、航空、冶金等领域。
成为各行业中不可缺少的结构材料，其主要特点如下：
1．优良的力学性能。尼龙的机械强度高，韧性好。
2．自润性、耐摩擦性好。尼龙具有很好的自润划性，摩擦系数小，从而，作为传动部件其使用寿命长。
3.优良的耐热性。如尼龙46等高结晶性尼龙的热变形温度很高，可在150℃下长期期使用。PA66经过
玻璃纤维增强以后，其热变形温度达到250℃以上。
4.优异的电绝缘性能。尼龙的体积电阻很高，耐击穿电压高，是优良的电气、电器绝缘材料。
5.优良的耐气候性。
6.吸水性。尼龙吸水性大，饱和吸水可达到3%以上。在一定程度影响制件的尺寸稳定性。